Eurostar Staramide PF005 PA6, 25% Glass Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide PF005 PA6, 25% Glass Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide PF005 is an 25% Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 6.5 % @Temperature 23.0 °C |
6.5 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 123 - 127 °C | 253 - 261 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 240 - 250 °C | 464 - 482 °F | |
| Zone 3 | 240 - 270 °C | 464 - 518 °F | |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Chevron Phillips mPact™ D449 HDPE Blown Film Resin (discontinued **)
- Overview of materials for Polyphenylene Sulfide (PPS) with PTFE Filler
- Overview of materials for Nylon 11 with 30% Glass Fiber Filler
- LyondellBasell Petrothene® NA960083 Low Density Polyethylene
- International Mold Steel Premium H13 Hot Work Die and Mold Steel
- Samyang Triloy® 210NHF Polymer Alloy, Flame Retardancy (Non-Halogen)
- Teknor Apex Telcar® TL-1402G Thermoplastic Elastomer
- Zhejiang Juner 301-G25 25% Glass Fibre Reinforced and Flammable Resistant
- ELM® TempFlex™ 0 to 100 Biodegradable Rail Curve Lubricant
- PolyOne Synprene® RT-3975 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved