ExxonMobil Exceed™ 350D65 LDPE/Hexene Tough Premium Liner Film Resin, 3.1 mil Film (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Exceed™ 350D65 LDPE/Hexene Tough Premium Liner Film Resin, 3.1 mil Film (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 350D65 resin have outstanding tensile, impact strength and puncture.Applications: Trash bags; Liners; General packaging. Data for film properties below based on 3.1 mil film.

Physical Properties	Metric	English	Comments
Density	0.917 g/cc	0.0331 lb/in³	Exxon Method
Thickness	78.7 microns	3.10 mil
Melt Flow	1.0 g/10 min	1.0 g/10 min	Exxon Method

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	9.00 MPa	1310 psi	ASTM D882
Film Tensile Strength at Yield, TD	9.20 MPa	1330 psi	ASTM D882
Film Elongation at Break, MD	620 %	620 %	ASTM D882
Film Elongation at Break, TD	630 %	630 %	ASTM D882
Secant Modulus, MD	0.216 GPa	31.3 ksi	ASTM D882
Secant Modulus, TD	0.245 GPa	35.5 ksi	ASTM D882
Coefficient of Friction	0.12	0.12	ASTM D1894
Elmendorf Tear Strength MD	1070 g	1070 g	ASTM D1922
Elmendorf Tear Strength TD	1220 g	1220 g	ASTM D1922
Elmendorf Tear Strength, MD	13.6 g/micron	345 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	15.5 g/micron	394 g/mil	ASTM D1922
Dart Drop	18.7 g/micron	474 g/mil	F50; ASTM D1709
Dart Drop Test	1470 g	3.24 lb	F50; ASTM D-1709
Film Tensile Strength at Break, MD	54.0 MPa	7830 psi	ASTM D882
Film Tensile Strength at Break, TD	53.0 MPa	7690 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	118 °C	244 °F	Exxon Method

Optical Properties	Metric	English	Comments
Haze	13.6 %	13.6 %	ASTM D1003
Gloss	59 %	59 %	45°, ASTM D-2457