ExxonMobil LD 317.09 Film Resin

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 317.09 Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 317 Series offer excellent impact strength, tensile properties, and heat sealability. Applications include ice bags, frozen food packaging, and other food packaging.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ExxonMobil Method
Vinyl Acetate Content 6.1 %
6.1 %
ExxonMobil Method
Thickness 50.8 microns
2.00 mil
Melt Flow 0.25 g/10 min
0.25 g/10 min
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.76 MPa
1270 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 7.45 MPa
1080 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 150 %
150 %
ASTM D882
Film Elongation at Break, TD 550 %
550 %
ASTM D882
Film Elongation at Yield, MD 7.5 %
7.5 %
ASTM D882
Film Elongation at Yield, TD 5.5 %
5.5 %
ASTM D882
Elmendorf Tear Strength, MD 3.15 g/micron
80.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 4.72 g/micron
120 g/mil
ASTM D1922
Dart Drop 8.66 g/micron
220 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 26.2 MPa
3800 psi
ASTM D882
Film Tensile Strength at Break, TD 26.9 MPa
3900 psi
ASTM D882
1% Secant Modulus, MD 138 MPa
20000 psi
ASTM D882
1% Secant Modulus, TD 161 MPa
23400 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 102 °C
216 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 12 %
12 %
ASTM D1003
Gloss 54 %
54 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer