ExxonMobil Label-Lyte™ 70LTR742 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Label-Lyte™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Label-Lyte™ 70LTR742 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A matte finish, coated, white, polypropylene film designed for use in demanding thermal transfer, pressure-sensitive label applications. It is also compatible with a wide range of water-based or solvent-based flexo, gravure, UV screen, and UV flexo ink systems. The adhesive side is coated to provide improved pressure-sensitive adhesive anchorage.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent print resolution and abrasion resistanceWide compatibility with the thermal transfer ribbonsExcellent bar code scannabilityExcellent static resistant propertiesFeatures:Static Resistant CoatedStatic Resistant Matte Coated Applications:Household and DetergentsIndustrialPaper Ream WrapPharmaceuticals Uses: Pressure Sensitive LabelsProcessing Method: Digital Offset (HP Indigo) Printing, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported, Thermal Transfer Printing, UV Flexographic Printing, UV Screen Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Thickness 61.0 microns
2.40 mil
ExxonMobil Method
Coating Weight 48.5 g/m²
30.3 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 170 %
170 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 55 %
55 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 1.60 GPa
232 ksi
MD; ExxonMobil Method
2.60 GPa
377 ksi
TD; ExxonMobil Method
Film Tensile Strength at Break, MD 105 MPa
15200 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 185 MPa
26800 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 4.0 %

@Temperature 135 °C,
Time 432 sec
4.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 2.0 %

@Temperature 135 °C,
Time 432 sec
2.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Gloss 10 %
10 %
45°; ExxonMobil Method
Transmission, Visible 20 %
20 %
ExxonMobil Method
Descriptive Properties Value Comments
Yield 14300 in2/lb
Copyright © lookpolymers.com All Rights Reserved