Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 1.60 GPa | 232 ksi | 4 mm thick;10.0 mm wide molded rod; ISO 178 |
Premix Thermoplastics PRE-ELEC® ESD 7120 PRE-ELEC ESD 7120 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 7120 has been developed for inject.. |
|||
Modulus of Elasticity | 1.60 - 17.0 GPa | 232 - 2470 ksi | Average value: 3.03 GPa Grade Count:30 |
Overview of materials for Polybutylene Terephthalate (PBT), Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Impact Grade". Each property range of values reported is minimum and m.. |
|||
Modulus of Elasticity | 1.60 - 7.30 GPa @Temperature 60.0 - 150 °C |
232 - 1060 ksi @Temperature 140 - 302 °F |
Average value: 3.70 GPa Grade Count:1 |
Overview of materials for Nylon 66, 40% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Mineral Filled". Specific grades with primary filler content between 35% and 44% are inclu.. |
|||
Modulus of Elasticity | 1.60 - 3.64 GPa | 232 - 528 ksi | Average value: 2.37 GPa Grade Count:6 |
Overview of materials for Nylon 12, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | ISO 527 |
GEHR Plastics PVDF-ELS Polyvinylidene Fluoride, Electrically Conductive Polyvinylidene fluoride shows a higher tensile strength, pressure resistance and dimensional stability than the related PTFE, but friction and insulation properties are lower. PVDF has a high mechan.. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | |
Lehmann & Voss LUVOCOM® TPE-0900 VP Thermoplastic elastomer, with carbon fiber Applications: Electrically conductive, suitable for continuous discharging of statically generated electricity.Improved wear behaviour, low warpage.Bearings, sleeves, sliding elements, chair rollers.. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | MD; ExxonMobil Method |
ExxonMobil Label-Lyte™ 65LTR741 OPP Film Product Description: A biaxially oriented, white opaque multi-layer polypropylene film with an expanded core, and coated with a proprietary static resistant coating on one side. The non-coated gloss.. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | MD; ExxonMobil Method |
ExxonMobil Label-Lyte™ 70LTR742 OPP Film Product Description: A matte finish, coated, white, polypropylene film designed for use in demanding thermal transfer, pressure-sensitive label applications. It is also compatible with a wide range .. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | ISO 527-1 |
Dow BETAMATE™ 1496 V Epoxy BETAMATE™ 1496 V is a one component, epoxy based adhesive especially developed for the body shop. The product has the following properties: Good rheology performance (Wash-out resistant, excelle.. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | MD; ExxonMobil Method |
ExxonMobil Label-Lyte™ 60LH538 OPP Film Product Description: A super white opaque polypropylene film face stock with a proprietary caviated core providing high yield and excellent opacity. The coated print surface provides exceptional ink.. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | ISO 178 |
Addiplast Addilene J 120 M10 Polypropylene Copolymer Low fluidity for extrusion or injectionInformation provided by Addiplast. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | Conditioned; ISO 178 |
Addiplast Addinyl A2 ZP40 Nylon 66, 40% Mineral Filled Mineral filled, increased thermal aging stabilityInformation provided by Addiplast. |
|||
Modulus of Elasticity | 1.60 - 2.10 GPa @Temperature 60.0 - 120 °C |
232 - 305 ksi @Temperature 140 - 248 °F |
Average value: 1.83 GPa Grade Count:1 |
Overview of materials for Polycarbonate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Molded". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Modulus of Elasticity | 1.60 - 2.20 GPa | 232 - 319 ksi | Average value: 1.90 GPa Grade Count:7 |
Overview of materials for Cellulose Acetate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate, Molded". Each property range of values reported is minimum and maximum values of appr.. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | ASTM D638 |
ITW Plexus Plexus™ MA340 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic and composites. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | Conditioned; ISO 178 |
Addiplast Addinyl B2H G15 Flame Retardant Nylon 6, 15% Glass Bead Flame retardant, 15% glass bead filled, with halogensInformation provided by Addiplast. |
|||
Modulus of Elasticity | 1.60 GPa | 232 ksi | Conditioned; ISO 178 |
Addiplast Addinyl PMD 20170 Nylon 66 GalvanizingInformation provided by Addiplast. |
|||
Modulus of Elasticity | 1.60 - 29.0 GPa | 232 - 4200 ksi | Average value: 8.94 GPa Grade Count:55 |
Overview of materials for Polytrimethylene Terephthalate (PTT) This property data is a summary of similar materials in the MatWeb database for the category "Polytrimethylene Terephthalate (PTT)". Each property range of values reported is minimum and maximum val.. |