Material Notes:
Powder Metallurgy BarDescription of Product: This specification covers molybdenum alloy (Molybdenum + 0.5% titanium + 0.1% zirconium) wrought bar produced from pressed and sintered powder metallurgy billet.Structure: Bars can be supplied in the recrystallized condition.Information provided by H.C. Starck.
Mechanical Properties Metric English Comments
Hardness, Vickers <= 215

@Load 10.0 kg
<= 215

@Load 22.0 lb
mid-radius, recrystallized bar, all sizes; DPH (10 kg)
230 - 285

@Load 10.0 kg,
Diameter 73.03 - 88.9 mm
230 - 285

@Load 22.0 lb,
Diameter 2.875 - 3.50 in
mid-radius; DPH (10 kg)
235 - 290

@Load 10.0 kg,
Diameter 47.63 - 73.03 mm
235 - 290

@Load 22.0 lb,
Diameter 1.875 - 2.875 in
mid-radius; DPH (10 kg)
240 - 300

@Load 10.0 kg,
Diameter 28.57 - 47.63 mm
240 - 300

@Load 22.0 lb,
Diameter 1.125 - 1.875 in
mid-radius; DPH (10 kg)
245 - 310

@Load 10.0 kg,
Diameter 22.2 - 28.57 mm
245 - 310

@Load 22.0 lb,
Diameter 0.875 - 1.125 in
mid-radius; DPH (10 kg)
255 - 320

@Load 10.0 kg,
Diameter 3.17 - 22.2 mm
255 - 320

@Load 22.0 lb,
Diameter 0.125 - 0.875 in
mid-radius; DPH (10 kg)
Tensile Strength >= 586 MPa

@Diameter 73.03 - 88.9 mm
>= 85000 psi

@Diameter 2.875 - 3.50 in
ASTM E-8
>= 621 MPa

@Diameter 47.63 - 73.03 mm
>= 90000 psi

@Diameter 1.875 - 2.875 in
ASTM E-8
>= 689 MPa

@Diameter 28.57 - 47.63 mm
>= 100000 psi

@Diameter 1.125 - 1.875 in
ASTM E-8
>= 758 MPa

@Diameter 22.2 - 28.57 mm
>= 110000 psi

@Diameter 0.875 - 1.125 in
ASTM E-8
>= 793 MPa

@Diameter 3.17 - 22.2 mm
>= 115000 psi

@Diameter 0.125 - 0.875 in
ASTM E-8
Tensile Strength, Yield >= 517 MPa

@Diameter 73.03 - 88.9 mm,
Strain 0.200 %
>= 75000 psi

@Diameter 2.875 - 3.50 in,
Strain 0.200 %
ASTM E-8
>= 552 MPa

@Diameter 47.63 - 73.03 mm,
Strain 0.200 %
>= 80000 psi

@Diameter 1.875 - 2.875 in,
Strain 0.200 %
ASTM E-8
>= 586 MPa

@Diameter 28.57 - 47.63 mm,
Strain 0.200 %
>= 85000 psi

@Diameter 1.125 - 1.875 in,
Strain 0.200 %
ASTM E-8
>= 655 MPa

@Diameter 22.2 - 28.57 mm,
Strain 0.200 %
>= 95000 psi

@Diameter 0.875 - 1.125 in,
Strain 0.200 %
ASTM E-8
>= 689 MPa

@Diameter 3.17 - 22.2 mm,
Strain 0.200 %
>= 100000 psi

@Diameter 0.125 - 0.875 in,
Strain 0.200 %
ASTM E-8
Elongation at Break >= 5.0 %

@Diameter 73.03 - 88.9 mm
>= 5.0 %

@Diameter 2.875 - 3.50 in
ASTM E-8
>= 10 %

@Diameter 28.57 - 47.63 mm
>= 10 %

@Diameter 1.125 - 1.875 in
ASTM E-8
>= 10 %

@Diameter 47.63 - 73.03 mm
>= 10 %

@Diameter 1.875 - 2.875 in
ASTM E-8
>= 15 %

@Diameter 22.2 - 28.57 mm
>= 15 %

@Diameter 0.875 - 1.125 in
ASTM E-8
>= 18 %

@Diameter 3.17 - 22.2 mm
>= 18 %

@Diameter 0.125 - 0.875 in
ASTM E-8
Component Elements Properties Metric English Comments
Carbon, C 0.010 - 0.040 %
0.010 - 0.040 %
Iron, Fe <= 0.010 %
<= 0.010 %
Molybdenum, Mo >= 99.2 %
>= 99.2 %
by difference
Nickel, Ni <= 0.0050 %
<= 0.0050 %
Nitrogen, N <= 0.0020 %
<= 0.0020 %
Sintered material
Oxygen, O <= 0.040 %
<= 0.040 %
Sintered material
Silicon, Si <= 0.0050 %
<= 0.0050 %
Titanium, Ti 0.40 - 0.55 %
0.40 - 0.55 %
Zirconium, Zr 0.060 - 0.12 %
0.060 - 0.12 %