Hexcel® HexWeb® ACG®-1/2 Honeycomb Aluminum Commercial Grade

Category Metal , Metal Foam, Mesh, or Honeycomb , Nonferrous Metal , Aluminum Alloy , 3000 Series Aluminum Alloy
Manufacturer Hexcel
Trade Name HexWeb®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® ACG®-1/2 Honeycomb Aluminum Commercial Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HexWeb® Aluminum Commercial Grade honeycomb is made from 3000 series aluminum alloy foil. An organic coating is applied to the foil which provides excellent protection against corrosive atmospheres. Five cell sizes and densities are availabe. The honeycomb is manufactured by bonding together sheets of aluminum foil which are expanded to form a cellular honeycomb configuration. The node bond adhesive is a thermosetting type, cured under heat and pressure with the honeycomb in the unexpanded or HOBE® (Honeycomb Before Expansion) condition. Slices are cut from the unexpanded material to specified thickness, or cell depth, and then expanded to final configuration.The honeycomb can be supplied either expanded or in HOBE slices. Any sheet thickness between 0.125 and 20 inches can be provided. The aluminum substrate can be perforated so that all cells will be vented in a slice as thin as 0.187 inches. The perforations of the HexWeb® ACG® foil allow outgassing of the adhesives used to bond panel facings. Nonperforated honeycomb is also available.Applications: HexWeb® ACG® is a commercial grade honeycomb core offering industrial designers the advantages of an all-metal honeycomb with long service life and resistance to fungus, moisture, and temperature. Uses include industrial tooling panels , architectural panels, shelving, storage tank covers, building walls, table and countertops.
Physical Properties Metric English Comments
Density 0.0368 g/cc
0.00133 lb/in³
Nominal
Mechanical Properties Metric English Comments
Compressive Yield Strength 1.31 MPa
190 psi
Bare
1.41 MPa
205 psi
Stabilized
Compressive Modulus 0.276 GPa
40.0 ksi
Stabilized
Shear Modulus 0.0965 GPa
14.0 ksi
Plate Shear, W Direction
0.193 GPa
28.0 ksi
Plate Shear, L Direction
Shear Strength 0.552 MPa
80.0 psi
Plate Shear, W Direction
0.965 MPa
140 psi
Plate Shear, L Direction