Hexcel® HexWeb® HRH-10 - 3/16 - 1.8 Aramid Fiber/Phenolic Resin Honeycomb

Category Other Engineering Material , Composite Core Material , Polymer , Thermoset , Aramid , Phenolic
Manufacturer Hexcel
Trade Name HexWeb®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® HRH-10 - 3/16 - 1.8 Aramid Fiber/Phenolic Resin Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation: Material-Cell Size-Density.Hexweb® HRH-10 is manufactured from NOMEX® aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the hexagonal or OX-Core® configuration, the block is dipped in phenolic resin. After curing the resin, slices are cut to the desired thickness. For special applications, such as air directionalizing, HexWeb® HRH-10 can be provided without the phenolic resin. Using this process, a wide range of cell sizes, paper thicknesses, and densities can be produced.Information provided by HexCel
Physical Properties Metric English Comments
Density 0.0288 g/cc
0.00104 lb/in³
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 0.655 MPa
>= 95.0 psi
Bare, min
>= 0.724 MPa
>= 105 psi
Stabilized, min
0.827 MPa
120 psi
Bare, typ
0.896 MPa
130 psi
Stabilized, typ
Compressive Modulus 0.0552 GPa
8.00 ksi
Stabilized, typ
Shear Modulus 0.0131 GPa
1.90 ksi
Plate Shear, W Direction, typ
0.0262 GPa
3.80 ksi
Plate Shear, L Direction, typ
Shear Strength >= 0.276 MPa
>= 40.0 psi
Plate Shear, W Direction, min
0.345 MPa
50.0 psi
Plate Shear, W Direction, typ
>= 0.517 MPa
>= 75.0 psi
Plate Shear, L Direction, min
0.621 MPa
90.0 psi
Plate Shear, L Direction, typ