Huntsman Rexell® L3106 Blown Film Extrusion LLDPE  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman Rexell® L3106 Blown Film Extrusion LLDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Linear-low density copolymer, cast film extrusion, FDA compliant.Features: Excellent processability with good sealing and optical properties.Applications: Blending resin and general purpose packaging.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)3.2.aFilm properties based on 0.95 guage (24 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 24.1 microns
0.950 mil
Melt Flow 6.6 g/10 min
6.6 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 560 %
560 %
ASTM D882
Film Elongation at Break, TD 690 %
690 %
ASTM D882
Secant Modulus, MD 0.110 GPa
16.0 ksi
ASTM D882
Secant Modulus, TD 0.124 GPa
18.0 ksi
ASTM D882
Elmendorf Tear Strength MD 270 g
270 g
ASTM D1922
Elmendorf Tear Strength TD 540 g
540 g
ASTM D1922
Elmendorf Tear Strength, MD 11.2 g/micron
284 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 22.4 g/micron
568 g/mil
ASTM D1922
Dart Drop 4.96 g/micron
126 g/mil
ASTM D1709
Dart Drop Test 120 g
0.265 lb
ASTM D1709
Film Tensile Strength at Break, MD 33.0 MPa
4790 psi
ASTM D882
Film Tensile Strength at Break, TD 17.0 MPa
2470 psi
ASTM D882
Optical Properties Metric English Comments
Haze 1.2 %
1.2 %
ASTM D1003
Gloss 90 %
90 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F