LATI Latamid 6 H2 G/30-V2HF PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 H2 G/30-V2HF PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-2 classified, halogens-based flame retardants and red phosphorous freeAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0060 cm/cm
0.0035 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0085 cm/cm
0.0065 - 0.0085 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 20.0 MPa

@Temperature 150 °C
 2900 psi

@Temperature 302 °F
35.0 MPa

@Temperature 120 °C
 5080 psi

@Temperature 248 °F
45.0 MPa

@Temperature 90.0 °C
 6530 psi

@Temperature 194 °F
70.0 MPa

@Temperature 60.0 °C
 10200 psi

@Temperature 140 °F
90.0 MPa

@Temperature 23.0 °C
 13100 psi

@Temperature 73.4 °F
Elongation at Break 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
3.6 %

@Temperature 60.0 °C
 3.6 %

@Temperature 140 °F
6.0 %

@Temperature 90.0 °C
 6.0 %

@Temperature 194 °F
7.8 %

@Temperature 120 °C
 7.8 %

@Temperature 248 °F
12 %

@Temperature 150 °C
 12 %

@Temperature 302 °F
Tensile Modulus 2.50 GPa

@Temperature 150 °C
 363 ksi

@Temperature 302 °F
3.00 GPa

@Temperature 120 °C
 435 ksi

@Temperature 248 °F
3.60 GPa

@Temperature 90.0 °C
 522 ksi

@Temperature 194 °F
5.50 GPa

@Temperature 60.0 °C
 798 ksi

@Temperature 140 °F
7.00 GPa

@Temperature 23.0 °C
 1020 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 110 °C
230 °F
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
Deflection Temperature at 1.8 MPa (264 psi) 165 °C
329 °F
Vicat Softening Point 210 °C

@Load 5.00 kg
 410 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
Oxygen Index 25 %
25 %
Glow Wire Test 850 °C

@Thickness 1.00 mm
 1560 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 575 V
575 V
A solution
Processing Properties Metric English Comments
Melt Temperature 240 - 250 °C
464 - 482 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa