LNP Thermocomp® EC-1006 EM Polyetherimide, Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® EC-1006 EM Polyetherimide, Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
Method A; ASTM D792
Water Absorption 0.10 %
0.10 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 230 MPa
33400 psi
ASTM D638
Tensile Strength, Yield 230 MPa
33400 psi
ASTM D638
Elongation at Break 1.5 %
1.5 %
ASTM D638
Elongation at Yield 1.5 %
1.5 %
ASTM D638
Tensile Modulus 23.3 GPa
3380 ksi
ASTM D638
Flexural Strength 310 MPa
45000 psi
ASTM D790
Flexural Modulus 19.2 GPa
2780 ksi
ASTM D790
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 34.7 kJ/m²
16.5 ft-lb/in²
ISO 180
Falling Dart Impact 6.30 J
4.65 ft-lb
ASTM D3763
Coefficient of Friction, Dynamic 0.52
0.52
vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static 0.48
0.48
vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor 149 x 10-8 mm³/N-M
74.0 x 10-10 in³-min/ft-lb-hr
40psi, 50ft/min; tested in accordance with LNP WI-0687
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 206 °C
403 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 360 - 366 °C
680 - 691 °F
Mold Temperature 121 - 149 °C
250 - 300 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi