Lanxess Pocan® KU 2-7209 Z 901510 PBT, 15% Glass Fiber

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Pocan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® KU 2-7209 Z 901510 PBT, 15% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, injection molding grade with 15% glass fibers, elastomer modified, UL 94V0 at 0.8 mm (all colors-in house test), UL-listed from 1.5mm thickness.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; Test Sim. to ISO 62
Melt Flow 31 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 31 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
ISO 527-1/-2
Elongation at Break 2.8 %
2.8 %
ISO 527-1/-2
Tensile Modulus 6.70 GPa
972 ksi
ISO 527-1/-2
Charpy Impact Unnotched 5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Vicat Softening Point 205 °C
401 °F
50°C/h 50N; ISO 306
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 IEC 60695-11-10
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Comparative Tracking Index 250 V
250 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 10724
Descriptive Properties Value Comments
Features High impact or high impact modified
Form Pellets
ISO Shortname ISO 7792-1-PBT,MFHPR,10-060,GF15; ISO 1043-PBT GF FR(17)
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved