Lubrizol ESTANE® 54610 Ester Based Thermoplastic Polyurethane

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol ESTANE® 54610 Ester Based Thermoplastic Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Good physical properties and chemical resistance and wide processing window for calendering.Uses: Melt coating/calendering, flat die/cast film extrusion.Available in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by Lubrizol.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Mechanical Properties Metric English Comments
Hardness, Shore A 82 - 88

@Time 5.00 sec
82 - 88

@Time 0.00139 hour
ASTM D2240
Tensile Strength 37.2 MPa
5400 psi
ASTM D412
Tensile Strength, Ultimate 37.2 MPa
5400 psi
ASTM D412/D638
Elongation at Break 620 %
620 %
ASTM D412/D638
100% Modulus 0.00530 GPa
0.769 ksi
ASTM D412
300% Modulus 0.00830 GPa
1.20 ksi
ASTM D412
Tear Strength 26.3 kN/m
150 pli
Trouser; ASTM D470
Graves Tear Strength 70.1 kN/m
400 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 2.5
2.5
H18, 1000g; ASTM D3389 B
Tensile Set 11 %
11 %
200% elongation
Thermal Properties Metric English Comments
Melting Point 120 °C
248 °F
DSC
Glass Transition Temp, Tg 120 °C
248 °F
DSC
Processing Properties Metric English Comments
Zone 1 171 °C
340 °F
Extrusion
Zone 2 177 °C
351 °F
Extrusion
Zone 3 182 °C
360 °F
Extrusion
Zone 4 188 °C
370 °F
Extrusion
Adapter Temperature 188 °C
370 °F
5, Extrusion
Die Temperature 188 °C
370 °F
Zone 1, 6, Extrusion
188 °C
370 °F
Zone 2, Extrusion
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Dew Point -40.0 °C
-40.0 °F