Lucas-Milhaupt BRAZE 716 (VTG) Grade 1 Silver Based Cadmium Free Filler Metal

Category Metal , Nonferrous Metal , Precious Metal , Silver Alloy , Solder/Braze Alloy
Manufacturer Lucas-Milhaupt
Trade Name BRAZE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lucas-Milhaupt BRAZE 716 (VTG) Grade 1 Silver Based Cadmium Free Filler Metal.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics: Braze 716 is a nickel modified silver copper eutectic filler metal. The addition of nickel renders this alloy somewhat more sluggish in flow characteristics than the eutectic composition but improve the wettability on ferrous alloys.On either silver, nickel, or copper base alloys Braze 716 exhibits a decrease in fluidity and an increase in remelt temperature, after brazing, due to the solution of some base metal in the filler metal. Specifications: This filler metal conforms to the following specifications: AMS 4766, AWS A5.8 BVAg-8b, Grade 1Information provided by Lucas-Milhaupt, Inc.
Physical Properties Metric English Comments
Density 10.0 g/cc
0.361 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength at Break 207 - 241 MPa
30000 - 35000 psi
Copper butt joint
241 - 276 MPa
35000 - 40000 psi
Nickel-Silver butt joint
241 - 345 MPa
35000 - 50000 psi
Brass butt joint
310 - 379 MPa
45000 - 55000 psi
1020 Steel butt joint
Elongation at Break 2.0 - 3.0 %
2.0 - 3.0 %
% in 2", Nickel-Silver butt joint
8.0 - 12 %
8.0 - 12 %
% in 2", 1020 Steel butt joint
10 - 19 %
10 - 19 %
% in 2", Copper butt joint
13 - 25 %
13 - 25 %
% in 2", Brass butt joint
Thermal Properties Metric English Comments
Melting Point 779.4 - 796.1 °C
1435 - 1465 °F
Solidus 779.4 °C
1435 °F
Melting Point
Liquidus 796.1 °C
1465 °F
Flow Point
Component Elements Properties Metric English Comments
Cadmium, Cd <= 0.0010 %
<= 0.0010 %
Carbon, C <= 0.0050 %
<= 0.0050 %
Copper, Cu >= 26.728 %
>= 26.728 %
Lead, Pb <= 0.0020 %
<= 0.0020 %
Nickel, Ni 0.30 - 0.70 %
0.30 - 0.70 %
Other, each <= 0.011 %
<= 0.011 %
Other, total 0.050 %
0.050 %
Phosphorous, P <= 0.0020 %
<= 0.0020 %
Silver, Ag 70.5 - 72.5 %
70.5 - 72.5 %
Zinc, Zn <= 0.0010 %
<= 0.0010 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000219 ohm-cm
0.00000219 ohm-cm
Processing Properties Metric English Comments
Processing Temperature 796.1 - 899 °C
1465 - 1650 °F
Brazing Range
Descriptive Properties Value Comments
Color Silver-White