LyondellBasell Hifaxâ„¢ A Thermoplastic Polyolefin Elastomer

Category Polymer , Film , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin
Manufacturer LyondellBasell
Trade Name Hifax™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Hifaxâ„¢ A Thermoplastic Polyolefin Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Hifaxâ„¢ CA 10 A is a thermoplastic polyolefin which has been developed for the extrusion and calendering of soft film and sheet. Thanks to its high rubber content "Hifax" CA 10 A features low stiffness, low hardness and good impact resistance. The base resin in CA10A meets the FDA requirements in the Code of Federal Regulations in 21 CFR 177.1520(a)(3)(iii) and (c)3.4 for olefin polymers. According to our Basell, all other ingredients used in the above formulation meet their respective FDA regulations and 21 CFR 177.1520(b). CA10A meets the FDA criteria for food contact, including cooking applications. CA10A can be used under conditions of use A through H listed in 21 CFR 176.170(c), Table 2(attached). However, CA10A can only be used in contact with food types I, II, III, IV-B, VI, VII, VIII and IX listed in 21 CFR 176.170(c), Table 1. Uses: Film, sheet, wall panels, wire and cable applicationsInformation provided by Basell.
Physical Properties Metric English Comments
Density 0.880 g/cc
0.0318 lb/in³
ISO 1183
Melt Flow 0.60 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.60 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Condition L; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 30
30
ISO 868
Tensile Strength, Yield 6.00 MPa
870 psi
ISO 527-1, -2
Elongation at Break 500 %
500 %
ISO 527-1, -2
Flexural Modulus 0.0800 GPa
11.6 ksi
ISO 178
Thermal Properties Metric English Comments
Melting Point 142 °C
288 °F
MTM 15902
Deflection Temperature at 0.46 MPa (66 psi) 43.9 °C
111 °F
ISO 75B-1, -2
Vicat Softening Point 56.1 °C
133 °F
A50 (50°C/h 10 N); ISO 306