Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
RheTech Products T12P600-01BG 12% Talc Reinforced Polypropylene Copolymer, General Purpose Black, Blow Molding Grade Applications: Flipper panelClose out panelSeat backsLoad floorInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
RheTech Products T12P600-430UVBG 12% Talc Reinforced Polypropylene Copolymer, UV Stabilized, Interior 848 Black, Blow Molding Grade Applications: Flipper panelsSeat backsLoad floorInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Riblene® FF 29 Low Density Polyethylene - Blown Film Extrusion Riblene FF 29 is a high molecular weight low density polyethylene (LDPE), suitable for blown film extrusion. Riblene FF 29 is characterized by a good melt strength leading to a good bubble stabilit.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A Condition L; ASTM D1238 |
Network Polymers NPP 30-007W Description: Homopolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
Melt Flow | 0.60 g/10 min @Load 3.80 kg, Temperature 200 °C |
0.60 g/10 min @Load 8.38 lb, Temperature 392 °F |
ASTM D 1238 |
SABIC Innovative Plastics Geloy EXGY30CP ASA Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region. |
|||
Melt Flow | 0.60 g/10 min @Load 3.80 kg, Temperature 200 °C |
0.60 g/10 min @Load 8.38 lb, Temperature 392 °F |
ASTM D 1238 |
SABIC Innovative Plastics Geloy FXTW30PE ASA Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
NOVA Chemicals Dylark® 238P20 High Performance Glass Filled Styrenic Very high modulus, High heat resistance, Excellent flow characteristics, Excellent adhesion to urethaneApplications: Instrument panel substrates, consoles, Cluster housing, interior trimInjection Sp.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg |
0.60 g/10 min @Load 4.76 lb |
ASTM D1238 |
Reliance Industries Relene W43006 Polyethylene Relene W43006 is a polyethylene grade recommended for insulation in jelly filled telecommunication cables. This grade contains a special stabilization system for improved thermal resistance. It is.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Clearflex® FF 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex FF 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Clearflex FF 106 are characterized by .. |
|||
Melt Flow | 0.60 - 0.90 g/10 min | 0.60 - 0.90 g/10 min | ±12% |
Kazanorgsintez 175-225 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg.. |
|||
Melt Flow | 0.60 - 0.90 g/10 min | 0.60 - 0.90 g/10 min | ±12% |
Kazanorgsintez 175-76 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg.. |
|||
Melt Flow | 0.60 g/10 min | 0.60 g/10 min | ASTM D1238 |
LyondellBasell Plexar® PX2246 Extrudable Tie-Layer Resin - Anhydride Modified HDPE General DescriptionPlexar® tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resin.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
nozzle diam 2.095 mm; ISO 1133 |
Inno-Comp INNOPOL® CS 3-8000 FR Flame Retardant Polypropylene Blend INNOPOL® CS 3-8000 FR is a flame retarded polypropylene compound based on a specific blend of polypropylene homo polymer and copolymer. This grade is available in natural and custom colored form... |
|||
Melt Flow | 0.60 - 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 - 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem LB 0117 LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba.. |
|||
Melt Flow | 0.60 - 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 - 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem LB 0120 BPS LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ISO 1133 |
LyondellBasell Adflexâ„¢ Q 100 F Polyolefin Description: Adflexâ„¢ Q 100 F is a thermoplastic polyolefin which has been developed for the extrusion of blown film, it is also suitable for sheet extrusion. Adflexâ„¢ Q 100 F features a ver.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
LyondellBasell Astryn 68F4-2 Polypropylene Homopolymer, 20% Talc Key Features: fractional melt flow, medium high modulus, mineral-filled, blow molding and extrusion grade polypropylene homopolymer, excellent impact and stiffness balance, good processabilityApplic.. |
|||
Melt Flow | 0.60 - 0.90 g/10 min @Load 5.00 kg, Temperature 230 °C |
0.60 - 0.90 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
Kureha KF Polymer 1300 PVDF Homopolymer KF Polymer is a fire-resistant engineering plastic which maintains the excellent performance of a fluoropolymer. It shows well-balanced molding processability similar to general-purpose resins. KF p.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
LyondellBasell Astryn SB572C Polypropylene Copolymer Key Features: fractional melt flow, medium modulus, extrusion grade polypropylene copolymer, good melt strength, good processabilityApplications: solar panelsDescription: Astryn SB572C fractional me.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis VL4470 High Density Polyethylene VL4470 is a high density polyethylene. Applications: Blown film, Rashel knitted and woven fabrics, and Stretch tape.Information provided by Borealis AG |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis VL4580 High Density Polyethylene VL4580 is a high density polyethylene. This grade is especially designed for monofilament production. Applications: ropes, twines, nets, straps and brushes.Information provided by Borealis AG |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LDPE LD 157CW Blown Low Density Polyethylene Resin Product Description: LD 157CW offer good mechanical properties as well as excellent opticals.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: YesAppl.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LDPE LD 157CW Wire & Cable Low Density Polyethylene Resin Product Description: LD 157CW is a medium density LDPE recommended for the production of Low Voltage power cable insulation, using the on-step silane cross0linking technology. The grade contains a h.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LDPE LD 364HE Low Density Polyethylene Resin Product Description: LD 364HE is an LDPE, offering a good combination of mechanical, optical and sealing properties.Availability: Africa & Middle East and Europe Additive: Antiblock: 1500 ppmSlip: .. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ExxonMobil Method |
ExxonMobil HD 7960.13 HMW Blown Film Resin Product Description: HD 7960.13 is a high molecular weight HDPE blown film resin. Films made from HD 7960.13 exhibit excellent impact and toughness properties, as well as high stiffness. HD 7960.13 .. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
Braskem TS7006 LDPE Blown Film Extrusion Polyethylene TS7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a combination of mechanical, optical, and stiffness properties. TS7006 has a l.. |
|||
Melt Flow | 0.60 - 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 - 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Breplast Bretene TS COR HF Film Light High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A. |
|||
Melt Flow | 0.60 g/10 min | 0.60 g/10 min | ASTM D1238 |
Westlake Hifor Xtreme SC74859 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme SC74859 polymer is a high strength linear low density polyethylene designed for blown film extrusion that contains no slip, high antiblock and high processing aid.Application/U.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Solvay Engineered Polymers SEQUEL® E2200 TPO
(discontinued **) Description: SEQUEL® E2200 thermoplastic olefinic elastomer (TPO) is designed for thermoformed exterior and interior applications that require low-temperature toughness and high rigidity. This pro.. |
|||
Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM-D1238 |
Braskem CP 743 HECO Polypropylene Heterophasic Copolymer CP 743 is a low melt flow rate heterophasic copolymer. It has broad molecular weight distribution and a general purpose additive package. CP 743 presents high melt strength, good processability, and.. |