Nilit RECONYL A Recycled nylon 6.6 for injection molding

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Nilit (formerly Frisetta Polymer)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit RECONYL A Recycled nylon 6.6 for injection molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Recycled nylon 6.6 for injection molding (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 2.0 - 3.0 %
2.0 - 3.0 %
ISO 62
Water Absorption at Saturation 7.0 - 8.0 %
7.0 - 8.0 %
ISO 62
Linear Mold Shrinkage 0.015 - 0.025 cm/cm
0.015 - 0.025 in/in
FRISETTA Test Method
Mechanical Properties Metric English Comments
Ball Indentation Hardness 135 MPa
19600 psi
ISO 2039-1
Tensile Strength at Break 75.0 MPa
10900 psi
ISO 527
Elongation at Break 8.0 %
8.0 %
ISO 527
Tensile Modulus 3.30 GPa
479 ksi
ISO 527
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Flexural Modulus 2.60 GPa
377 ksi
ISO 178
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
DIN 53453
NB
NB
ISO 179/1eU
4.00 J/cm²

@Temperature -40.0 °C
 19.0 ft-lb/in²

@Temperature -40.0 °F
 DIN 53453
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
DIN 53453
0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 256 °C
493 °F
ISO 3146 DSC
Maximum Service Temperature, Air 90.0 °C
194 °F
Continuous; FRISETTA Test Method
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
ISO 75