Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 80.0 - 110 MPa | 11600 - 16000 psi | ASTM D790-03 |
Proto3000 Objet Digital Materials™ DM_Grid_7523 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide t.. |
|||
Flexural Strength | 80.0 - 110 MPa | 11600 - 16000 psi | ASTM D790-03 |
Proto3000 Objet FullCure720 Transparent Prototyping Polymer Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid .. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP BX03658N SAN LNP* LUBRICOMP* BX03658N is a compound based on SAN resin containing proprietary fillers. Added features of this grade include: Wear Resistant, Tight Dimensional Tolerances, good for Water Meter A.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DL003 PC (Asia Pacific) LNP LUBRICOMP* DL003 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
Hexion Bakelite™ PF 12404 Phenolic Formaldehyde Resin, High Surface Quality, Low Shrinkage
(discontinued **)& Phenolic molding compound, inorganically/organically filled, good dimensional stability, low shrinkage.Application areas: Housing parts for gas meter.Information provided by Bak AGBak AG became a pa.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | |
Lehmann & Voss LUVOCOM® 1500-8299 Polysulfone, with PTFE, lubricant modified Applications: Isotropic shrinkage characteristics.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Control disks, ca.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | |
Lehmann & Voss LUVOCOM® 50-8479/BL-1 Polycarbonate, unreinforced Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Isotropic shrinkage characteristics.Reduced moment of inertia .. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | 2mm/min; ASTM D790 |
Kingfa JH950-502 Low-temperature Resistant & Flame Retardant PC/ABS Alloy Features:UL V-0 @ 3.2mmExcellent balance propertiesGood low temperature resistanceGood normal/low temperature impact strengthGood surfaceApplications:ControllerPlugSocketShell of ammeterInformation .. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | 2mm/min; ASTM D790 |
Kingfa MAC-301 PC/ABS Alloy Features:Excellent balance propertiesGood impact strengthGood processing propertiesSuit for electro-platingApplications:Injection moldingHousehold applianceAutomobile interior/exterior trim partsTel.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
Kolon KOCETAL® LF301 Wear Modified Acetal Resin Special polymer added, improved wear property. Applications: Products for low noise and precision gear. Information provided by API-Kolon. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | 3.5%; ISO 178 |
GEHR Plastics PVDF Polyvinylidene Fluoride Polyvinylidene fluoride shows a higher tensile strength, pressure resistance and dimensional stability than the related PTFE, but friction and insulation properties are lower. PVDF has a high mechan.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax CCP PBT 1100-211X Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1100-211L Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 - 85.0 MPa | 11600 - 12300 psi | ASTM D790 |
Loxim 600 00HB Polycarbonate/Polybutylene Terephthalate Information provided by Loxim Industries |
|||
Flexural Strength | 80.0 MPa | 11600 psi | |
Momentive Performance Materials Boralloy® PBN Pyrolytic Boron Nitride Boralloy® Pyrolytic Boron Nitride (PBN) is an anisotropic, high-temperature ceramic which exhibits a unique combination of high electrical resistance and good thermal conductivity. This non-toxi.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | |
Lehmann & Voss LUVOCOM® 50/TF/15/BK Polycarbonate, with PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Improved friction and wear behaviour. Emergency running proper.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp JL003 PES LNP* Lubricomp* JL003 is a compound based on Polyethersulfone resin containing PTFE.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | DIN 54352 |
Schwartz Technical Plastics LAMINEX® 2100 Cotton Fabric, Phenolic Resin Impregnated Application: bearing shells and bearing collarsInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
Polyram PlusTek PA841 Nylon 6.6, Impact Modified Impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
Polyram PlusTek RA843 Nylon 6.6, Impact Modified Impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
Toyobo VYLOPET® EMC605P PBT/PET Alloy, Anti-microbial Applications: Gas equipment partsFeatures: Good anti-microbialGood appearanceFlame resistantInformation provided by Toyobo. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | cond.; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 GF15 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 15% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® 302-G0 PBT Resin Flame retardant, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
Mitsubishi Xantar® MX 1004 Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances wher.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
Unitika EX-1020K PA6, Dry Conducting nylonInformation provided by Unitika Ltd. |