Plastcom SLOVAMID® 6 GF 30 AS PA6 reinforced with glass fiber, anti-static agent

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID® 6 GF 30 AS PA6 reinforced with glass fiber, anti-static agent.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6 for injection molding, reinforced with 30% glass fiber, contains antistatic agent for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, gears, covers of electric tools, automobile mirror housings, cooling screws of blowers, electromotors, bearing parts in the automotive industry. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
STN EN ISO 1183-1
Filler Content 30 %
30 %
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
STN EN ISO 294-4
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 175 MPa
25400 psi
STN EN ISO 527-2
Elongation at Break 3.0 %
3.0 %
STN EN ISO 527-2
Tensile Modulus 9.80 GPa
1420 ksi
STN EN ISO 527-2
Flexural Strength 220 MPa
31900 psi
STN EN ISO 178
Flexural Modulus 8.60 GPa
1250 ksi
STN EN ISO 178
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -20.0 °C
28.6 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
7.00 J/cm²

@Temperature 23.0 °C
33.3 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.800 J/cm²

@Temperature -20.0 °C
3.81 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
STN EN ISO 75-2 (A)
Vicat Softening Point 250 °C
482 °F
STN EN ISO 306
Flammability, UL94 HB
HB
Glow Wire Test 650 °C

@Thickness 3.00 mm
1200 °F

@Thickness 0.118 in
STN EN 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
STN 34 6460
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
STN 34 6460
Dielectric Strength 35.0 kV/mm
889 kV/in
STN EN 60243-2
Comparative Tracking Index 350 V
350 V
STN EN 60112
Processing Properties Metric English Comments
Melt Temperature 240 - 270 °C
464 - 518 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 3344
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi