Plastcom SLOVAMID 6 T 30 TS PA6, 30% mineral filling

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID 6
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID 6 T 30 TS PA6, 30% mineral filling.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesDecreased shrinkage against the BT types, increased heat application. Increased modulus in tension - strength of the material. PA matrix reduction. PA for injection moulding with the content of 30% micromilled talc. Delivered in natural mode and in the full RAL colour scale.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
Viscosity Measurement 0.84 - 0.85
0.84 - 0.85
Linear Mold Shrinkage 0.0085 cm/cm
0.0085 in/in
Linear Mold Shrinkage, Transverse 0.0084 cm/cm
0.0084 in/in
Melt Flow 3.0 g/10 min

@Load 0.325 kg,
Temperature 270 °C
3.0 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
Elongation at Break 8.0 %
8.0 %
Tensile Modulus 5.75 GPa
834 ksi
Flexural Strength 125 MPa
18100 psi
Flexural Modulus 1.45 GPa
210 ksi
Charpy Impact Unnotched 2.80 J/cm²

@Temperature -20.0 °C
13.3 ft-lb/in²

@Temperature -4.00 °F
4.20 J/cm²

@Temperature 23.0 °C
20.0 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.100 J/cm²

@Temperature -20.0 °C
0.476 ft-lb/in²

@Temperature -4.00 °F
0.300 J/cm²

@Temperature 23.0 °C
1.43 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Vicat Softening Point 210 °C
410 °F
B
Flammability, UL94 HB
HB
Glow Wire Test 650 °C
1200 °F
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi