Plastcom SLOVAMID 6/66 CF 30 PA6/66, 30% carbon fibre

Category Polymer , Thermoplastic , Nylon , Nylon 6/66
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID 6/66
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID 6/66 CF 30 PA6/66, 30% carbon fibre.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesPA 6/66 for injection moulding, chemically strengthened with 30% of carbon fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry. Delivered in black mode.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
Viscosity Measurement 0.89 - 1.04
0.89 - 1.04
Linear Mold Shrinkage 0.0089 cm/cm
0.0089 in/in
Linear Mold Shrinkage, Transverse 0.0104 cm/cm
0.0104 in/in
Melt Flow 1.0 g/10 min

@Load 0.325 kg,
Temperature 270 °C
1.0 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 220 MPa
31900 psi
Elongation at Break 2.0 %
2.0 %
Tensile Modulus 19.5 GPa
2830 ksi
Flexural Strength 330 MPa
47900 psi
Flexural Modulus 18.0 GPa
2610 ksi
Charpy Impact Unnotched 4.50 J/cm²

@Temperature 23.0 °C
21.4 ft-lb/in²

@Temperature 73.4 °F
5.00 J/cm²

@Temperature -20.0 °C
23.8 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.400 J/cm²

@Temperature -20.0 °C
1.90 ft-lb/in²

@Temperature -4.00 °F
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 220 - 260 °C
428 - 500 °F
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
Vicat Softening Point 205 °C
401 °F
B
Processing Properties Metric English Comments
Melt Temperature 280 - 310 °C
536 - 590 °F
Mold Temperature 90.0 - 120 °C
194 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.10 %
0.10 %
Injection Pressure 100 - 150 MPa
14500 - 21800 psi