Plenco 2567 Phenolic, Granular, Injection Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Resole, Wood Filled
Manufacturer Plenco (Plastics Engineering Company)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 2567 Phenolic, Granular, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PLENCO 02567 is a general purpose, organic filled phenolic molding compound offering excellent cosmetic characteristics as typically required for vacuum metalized closures. UL recognized under component file E40654. 02567 is available in black, brown, or red color. 02567 Black is not intended for electrical insulating applications.Information supplied by Plenco.
Physical Properties Metric English Comments
Bulk Density 0.580 g/cc
0.0210 lb/in³
ASTM D1895
Density 1.36 g/cc
0.0491 lb/in³
ASTM D792
Water Absorption 0.52 %
0.52 %
ASTM D570
Linear Mold Shrinkage 0.0069 cm/cm
0.0069 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell E 78
78
ASTM D785
Tensile Strength, Ultimate 69.0 MPa
10000 psi
ASTM D638
Elongation at Break 1.26 %
1.26 %
ASTM D638
Tensile Modulus 6.60 GPa
957 ksi
ASTM D638
Flexural Strength 105 MPa
15200 psi
ASTM D790
Flexural Modulus 6.70 GPa
972 ksi
ASTM D790
Compressive Strength 209 MPa
30300 psi
ASTM D695
Izod Impact, Notched 0.200 J/cm
0.375 ft-lb/in
ASTM D256
Charpy Impact, Notched 0.182 J/cm²
0.866 ft-lb/in²
ASTM D256
Impact 116
116
J/m Drop Ball Impact; PLENCO
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 190 °C
374 °F
Heat Resistance; ASTM D570D
Deflection Temperature at 1.8 MPa (264 psi) 178 °C
352 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Shrinkage 0.51 %
0.51 %
72 hr, 120ºC; ASTM D1299
Electrical Properties Metric English Comments
Comparative Tracking Index 175 V
175 V
ASTM D3638