Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 105 MPa | 15200 psi | ASTM D790 |
Plaskolite Optix® CA-71 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. High heat resistance, medium flow. |
|||
Flexural Strength | 105 MPa | 15200 psi | ASTM D790 |
Plaskolite West Optix® CA-80 General Purpose Acrylic Resin Extrusion Grade Pellets. Unlubricated version of CA-81. Highest Molecular weight. |
|||
Flexural Strength | 105 MPa | 15200 psi | |
Plastcom SLOVASTER® B1 GF 6/2 PBT reinforced with 6% glass fibre Features: PBT for injection moulding, chemically reinforced with 6 % glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bendi.. |
|||
Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
Nilit FRIANYL B63 KV25 Nylon 6 for injection molding, 25% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | <= 105 MPa | <= 15200 psi | ISO 178 |
Polykemi AB SCANAMID 66 A33^E Nylon 66, Modified Information provided by Polykemi AB |
|||
Flexural Strength | <= 105 MPa | <= 15200 psi | ISO 178 |
Polykemi AB SCANTEC PC S85R V0 Polycarbonate, Flame Retardant Information provided by Polykemi AB |
|||
Flexural Strength | 105 MPa | 15200 psi | 2mm/min; ASTM D790 |
Kingfa JH710 G10 Flame Retardant & 10% Glass Reinforced PC Features:Environmental friendly flame retardantUL V-0 @ 1.6mmHigh mechanical strengthGood size stability, good surfaceSuitable for exact moldingApplications:CD-ROM, DVDPrinter, photocopier cabinetSc.. |
|||
Flexural Strength | 105 MPa | 15200 psi | 2mm/min; ASTM D790 |
Kingfa PA66-ROW Halogen-free, Flame Retardant PA66 Features:Flame retardantHigh mechanical strengthHigh heat resistanceGood electric propertiesNo bloomingApplications:Injection moldingConnectors, linkersRelay, bobbins, plugsHousehold appliance parts.. |
|||
Flexural Strength | 105 MPa | 15200 psi | 1.5 mm/min; ISO 178:2001 |
Global EPP PA 6C HS BLUE Cast Polyamide 6 + UV and Heat Stabilizers Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
Flexural Strength | 105 MPa | 15200 psi | 1.5 mm/min; ISO 178:2001 |
Global EPP PA 6C WFN Cast Polyamide 6 + Wax Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
Kuraray Genestarâ„¢ N1001A-M41 Nylon Low friction unreinforced injection grade. Main Features:Low friction coefficientHigh impact strengthExamples of applications are:Friction and wear applicationGear and wheel |
|||
Flexural Strength | 105 MPa | 15200 psi | |
Lehmann & Voss LUVOCOM® 1105-7714 PEEK, with PTFE, lubricant modified, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Flexural Strength | 105 MPa | 15200 psi | |
Lehmann & Voss LUVOCOM® 80-8030 Polyacetal-copolymer, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically .. |
|||
Flexural Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL V03550 PPE+HIPS (Europe-Africa-Middle East) Noryl* V03550 is a 35% milled fibre reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly LNP* THERMOCOMP* KF002L is a compound based on Acetal Homopolymer resin containing 10% Glass Fiber. Added features of this material include: Low Extractible. |
|||
Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly (Asia Pacific) LNP* Thermocomp* KF002L is a compound based on Acetal Homopolymer resin containing Glass Fiber. Added features of this material include: Low Extractible. |
|||
Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp OK006 PPS - Linear LNP* Thermocomp* OK006 is based on a Linear Polyphenylene Sulfide (PPS) containing Talc.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL CTI2550 PPE+HIPS (Europe-Africa-Middle East) NORYL CTI2550 is a glass/mineral filled material with a Vicat B/120 of 160 °C according ISO 306. |
|||
Flexural Strength | 105 MPa | 15200 psi | ISO 178-93 |
Wellman Wellamid® NY1599-BK11 Unfilled Nylon 66 Description: Unfilled Nylon 66Information provided by Wellman. |
|||
Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
Polyram RamTal PMH2010 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 10.Information provided by Polyram. |
|||
Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
Polyram RamTough PZ506 Polycarbonate, UV Stabilized, Flame Retardant UV stabilized, flame retardant polycarbonate for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 105 MPa | 15200 psi | |
Toyobo ECOVYLOPET® EMC2301E PET Bottle Recycling Grade, 15% Filler Reinforced Features: PET Bottle Recycling Grade, 15% Filler Reinforced, Modified TypeApplications: Automobile engine head coversHot platesVending machine partsUmbrella ribsInformation provided by Toyobo. |
|||
Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
Eurostar Starflam R10002E PA66/6, Injection Molded Starflam R10002E is a Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant, Polyamide 66/Polyamide 6 Injection Molding Resin (also known as R1000Z220EM)Information provided by Polymer Te.. |
|||
Flexural Strength | 105 MPa @Temperature 93.0 °C |
15200 psi @Temperature 199 °F |
ASTM Test |
BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Dry) Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a
balance of st.. |
|||
Flexural Strength | 105 MPa | 15200 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® 551-GT30S PBT Resin Glass fiber and mineral filled, flame retardant, low warpage, superior electrical performanceInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 105 MPa | 15200 psi | |
Abatron AboCast 8502-7/AboCure 8502-7 Colorless, Low-Exotherm Epoxy Casting Compound AboCast 8502-7/AboCure 8502-7 is a rigid, heat cured, colorless, low-exotherm epoxy casting compound for larger masses. It is a 2-component structural and dielectric liquid system with extremely low.. |
|||
Flexural Strength | 105 MPa | 15200 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® MN-401 PA6 Resin Good toughnessInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 105 MPa | 15200 psi | |
Lehmann & Voss LUVOCOM® 1700-7903 PPO, with glass fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance r.. |
|||
Flexural Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
Sax Polymers SAXALEN PPC345G30 Polypropylene Copolymer, 30% Glass Filled SAXALEN PPC345G30 is a 30% glass filled Polypropylene - Copolymer intended for injection molding.Information provided by SAX Polymers |