Polimeri Europa KOBLEND PCA PD 935 G4 PC+ABS, 20% Glass Fiber  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa KOBLEND PCA PD 935 G4 PC+ABS, 20% Glass Fiber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Symbol according to ISO 1043/1/2: PC+ABS (GF) Injection moulding grade, reinforced with 20% glass fibres, high stiffness, very good dimensional stability. Main application fields: structural non aesthetic parts in the automotive industry, electro-mechanical componentsFilled. Suitable for Injection Molding. Supplied as pellets.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
Water Absorption 0.60 %
0.60 %
Melt Flow 11 g/10 min

@Load 5.00 kg,
Temperature 260 °C
11 g/10 min

@Load 11.0 lb,
Temperature 500 °F
cm³/10 min
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 85.0 MPa
12300 psi
5 mm/min
Elongation at Break 3.0 %
3.0 %
5 mm/min
Tensile Modulus 6.40 GPa
928 ksi
1 mm/min
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 20.0 °C
16.7 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 133 °C
271 °F
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Vicat Softening Point 132 °C
270 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 2.8

@Frequency 1e+6 Hz
2.8

@Frequency 1e+6 Hz
2.9

@Frequency 100 Hz
2.9

@Frequency 100 Hz
Dielectric Strength 27.0 kV/mm
686 kV/in
Dissipation Factor 0.0020

@Frequency 100 Hz
0.0020

@Frequency 100 Hz
0.010

@Frequency 1e+6 Hz
0.010

@Frequency 1e+6 Hz
Comparative Tracking Index 250 V
250 V