SABIC Innovative Plastics Valox® 420R PBT (Asia Pacific)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 420R PBT (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% GR, ex strength/stiffness/dimensional stability; heat resistance. Appliance handles, spotlights, electric motors, etc. Internal mold release.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.53 g/cc
1.53 g/cc
ASTM D 792
Water Absorption 0.060 %

@Time 86400 sec
0.060 %

@Time 24.0 hour
ASTM D 570
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 1.50 - 3.20 mm
0.0030 - 0.0050 in/in

@Thickness 0.0591 - 0.126 in
SABIC Method
0.0050 cm/cm

@Thickness 3.20 mm
0.0050 in/in

@Thickness 0.126 in
SABIC Method
0.0050 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 1.50 - 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.0591 - 0.126 in
SABIC Method
0.0060 - 0.0090 cm/cm

@Thickness 3.20 - 4.60 mm
0.0060 - 0.0090 in/in

@Thickness 0.126 - 0.181 in
SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D 785
Tensile Strength at Break 119 MPa
17300 psi
Type I, 5 mm/min; ASTM D 638
Flexural Yield Strength 189 MPa
27400 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 7.58 GPa
1100 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.850 J/cm

@Temperature 23.0 °C
1.59 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 8.01 J/cm

@Temperature 23.0 °C
15.0 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
14.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
25.2 µm/m-°C

@Temperature 60.0 - 138 °C
14.0 µin/in-°F

@Temperature 140 - 280 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 215 °C

@Thickness 6.40 mm
419 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 6.40 mm
405 °F

@Thickness 0.252 in
unannealed; ASTM D 648
UL RTI, Electrical 140 °C
284 °F
UL 746B
UL RTI, Mechanical with Impact 140 °C
284 °F
UL 746B
UL RTI, Mechanical without Impact 140 °C
284 °F
UL 746B
Flammability, UL94 HB

@Thickness 0.830 mm
HB

@Thickness 0.0327 in
UL 94
Oxygen Index 19 %
19 %
LOI; ASTM D 2863
Electrical Properties Metric English Comments
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
3.7

@Frequency 1.00e+6 Hz
ASTM D 150
3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
ASTM D 150
Dielectric Strength 18.7 kV/mm

@Thickness 3.20 mm
475 kV/in

@Thickness 0.126 in
in air; ASTM D 149
24.8 kV/mm

@Thickness 1.60 mm
630 kV/in

@Thickness 0.0630 in
in oil; ASTM D 149
Dissipation Factor 0.0020

@Frequency 100 Hz
0.0020

@Frequency 100 Hz
ASTM D 150
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
ASTM D 150
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten, PLC code 5; ASTM D 495
Comparative Tracking Index >= 600 V
>= 600 V
PLC code 0; UL 746A
Descriptive Properties Value Comments
High Voltage Arc Resistance {PLC), PLC Code 1
UL 746A