Polymer Resources PC-G20-[color]-WS Polycarbonate, 20% Glass Reinforced

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC-G20-[color]-WS Polycarbonate, 20% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
ASTM D955
Melt Flow 4.0 - 10 g/10 min
4.0 - 10 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 107 MPa
15500 psi
ASTM D638
Flexural Strength 112 MPa
16200 psi
ASTM D790
Flexural Modulus 5.00 GPa
725 ksi
ASTM D790
Izod Impact, Notched 0.641 J/cm
1.20 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
285 °F
ASTM D648
Flammability, UL94 V-2
V-2
1/16 in
V-0
V-0
1/8 in
Processing Properties Metric English Comments
Rear Barrel Temperature 293 - 316 °C
560 - 600 °F
Middle Barrel Temperature 304 - 327 °C
580 - 620 °F
Front Barrel Temperature 316 - 338 °C
600 - 640 °F
Melt Temperature 302 - 329 °C
575 - 625 °F
Mold Temperature 82.2 - 116 °C
180 - 240 °F
Drying Temperature 118 - 124 °C
245 - 255 °F
Dry Time 3 - 4 hour
3 - 4 hour