- Polymer Property : Melt Flow = 4.0 g/10 min
Polymer Property : Melt Flow = 4.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Plastcom PLASTAMID® 6 BT N 32 B/IM PA6 Basic type PA 6 for injection molding, compounding, for general use. Use: automotive, engineering, electrical and consumer goods industry - electrical tools, fasteners, clamps, hobby tools, toys. De.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A; ASTM D1238 |
| PolyOne Maxxam™ FR MF5210-0301 DK GRAY 2451 Polypropylene, Unspecified (PP, Unspecified) Information provided by PolyOne |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A; ASTM D1238 |
| PolyOne Maxxam™ NT-818.G002-1000 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Melt Flow | 4.0 g/10 min @Load 0.325 kg, Temperature 270 °C |
4.0 g/10 min @Load 0.716 lb, Temperature 518 °F |
|
| Plastcom SLOVAMID 66 BT TS PA66, basic type, thermal stability FeaturesModified for general use, with excellent manufacturing properties, characterized by high strength and toughness also at minus temperatures. Used in automotive, electrical, engineering and co.. |
|||
| Melt Flow | 4.0 - 12 g/10 min @Load 2.16 kg, Temperature 250 °C |
4.0 - 12 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TPSF-FRG30 Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced, Flame Retardant Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced, Flame RetardantProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, .. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products G30P100-00 30% Glass Fiber Reinforced Polypropylene, Natural Applications: Fender apronsUnderhood componentsStructural componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 4.0 g/10 min @Load 21.6 kg, Temperature 190 °C |
4.0 g/10 min @Load 47.6 lb, Temperature 374 °F |
without Catalyst MB addition; Internal Method |
| Solvay Specialty Polymers Cogegum® GFR/340-HP Polyolefin, Unspecified
(Unverified Data**) Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a polyolefi.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
|
| LG Chemical LUPOY HR-5006A Heat Resistant PC/ABS Alloy, Unreinforced, Weather Resistant Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos H04G-00 Polypropylene Homopolymer This is a controlled rheology general purpose homopolymer polypropylene. This grade is designed to meet the processing and physical property requirements of film and profile extrusion applications... |
|||
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| GRECO ISOPAK 547HF ABS Resin High Flow GradeInformation provided by Greater Eastern Resins Industrial Co., Ltd. |
|||
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE A 4002 BLK Multi-Flex® A 4002 is based on Shell's Kraton G polymer and is suitable for soft touch applications for the automotive industry. It exhibits excellent paintibility adhesion. Multi-Flex TPE cont.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
4.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Kureha KF Polymer 2950 PVDF Copolymer KF Polymer is a fire-resistant engineering plastic which maintains the excellent performance of a fluoropolymer. It shows well-balanced molding processability similar to general-purpose resins. KF p.. |
|||
| Melt Flow | 4.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| MRC Polymers NAXELL™ PC110VL Polycarbonate, Very Low MFR • Available in natural and custom colors• Can be UV Stabilized• Internal and external lubricants can be addedInformation provided by MRC Polymers Inc. |
|||
| Melt Flow | 4.0 g/10 min @Load 21.6 kg, Temperature 190 °C |
4.0 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
| Solvay Specialty Polymers Cogegum® GFR/340-HP Polyolefin Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound. Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a poly.. |
|||
| Melt Flow | 4.0 - 10 g/10 min | 4.0 - 10 g/10 min | ASTM D1238 |
| Shuman FR310 Utility Black PC/ABS Alloy, Flame Retardant Excellent flame retardancy, good impact strength, easy processability, good surface gloss, good chemical resistance, self extinguishing Formerly Shuman FR705 ABS/PC AlloyInformation provided by Shum.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg |
4.0 g/10 min @Load 4.76 lb |
ISO 1133 |
| SIDPEC EGYPTENE® HD 3840 UA MDPE Rotational Molding Applications:Rotational items: tanks, containers, etc...Injection molded technical parts and closureInformation provided by Interchim s.r.l., official distributor of Sidi Kerir Petrochemicals Co. (S.. |
|||
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | 2.16/190; ASTM D1238 |
| A. Schulman SUPERLINEAR™ XL 0370 Rotational Molding Resin DescriptionSuperlinear XL 0370 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used.. |
|||
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133H |
| Total PS CPDS FT875 Flame Retardant Polystyrene POLYSTYRENE (PS) COMPOUND (CPDS) FT875 is a high impact, halogen free flame retardant polystyrene. PS CPDS FT875 offers high heat stability and is recommended for the manufacturing of articles whic.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RCP 770C/CW DescriptionPolyflam® RCP 770C/CW is a flame-retardant concentrate based in low-density polyethylene that features excellent dispersion and processing stability up to 550°F.ApplicationRCP 770 C/CW.. |
|||
| Melt Flow | 4.0 - 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 - 6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| RTP Company RTP 155 A Polypropylene (PP) Mineral - Flame Retardant - Non-PBB/PBDE - UL94 V-0 |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RCP 500 C DescriptionPolyflam® RCP 500C is an economical flame-retardant concentrate based in low-density polyethylene that features excellent dispersion and processing stability up to 550°F. ApplicationRC.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RCP 505C Flame Retardant Concentrate Based In Low-Density Polyethylene Information provided by A. Schulman. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polyram RamOfin PPH301G6NT Polypropylene, 30% Glass Fiber 30% Glass fiber reinforced polypropylene for injection molding applications. Approved and listed by WRAS Potable Water.Information provided by Polyram. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 3491 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3491 is a low water carry over homopolymer polypropylene, designed for high speed extrusion.Information provided by A. Schulman. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
condition E; ASTM D1238 |
| DuPont™ Surlyn® PC350 Ionomer Resin, Highest Clarity, Sodium Surlyn® PC350 luxury molding resin is a "select" grade of Surlyn® 8945, controlled to achieve the highest possible optical clarity in molded perfume jars and caps, while being optimized for proces.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| ExxonMobil PP5722E1 Polypropylene Copolymer Product Description: A medium flow homopolymer resin designed for mono-oriented products like stretched tapes and monofilament.Availability: Asia Pacific Features:Good Gauge ControlGood Processabil.. |
|||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg |
4.0 g/10 min @Load 4.76 lb |
|
| Dow HDPE 04452N High Density Polyethylene DOW HDPE 04452N resin is a narrow molecular weight distribution copolymer designed to offer good stress crack resistance and stacking strength with excellent impact strength. This resin has moderate.. |
|||
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Chi Mei Polyrex® PG-80 Polystyrene High strength |
|||
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
|
| BASF Polystyrol® 475 K Impact Grade Polystyrene (Europe) Normal flowing, high-impact grade with particularly good creep strength.Data was collected by ISO methods and provided by BASF. |
|||
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | Condition L; ASTM D1238 |
| Asahi Kasei Delpet® 60N Acrylic Molding Compound 60N is a medium grade of heat resistance and mechanical strength, allowing injection molding through relatively small gates and runners. General Delpet® qualities include attractive transparency, .. |
|||