Polymer Resources PC/ABS-FRG5 Flame Retardant PC/ABS Alloy, 5% Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC/ABS-FRG5 Flame Retardant PC/ABS Alloy, 5% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC/ABS Alloy, Flame Retardant, 5% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 15 - 35 g/10 min @Load 5.00 kg, Temperature 250 °C |
15 - 35 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.9 MPa | 8400 psi | ASTM D638 |
| Tensile Strength, Yield | 59.3 MPa | 8600 psi | ASTM D638 |
| Flexural Strength | 98.6 MPa | 14300 psi | ASTM D790 |
| Flexural Modulus | 2.69 GPa | 390 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.3 °C | 173 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0626 in |
|
| V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 224 - 257 °C | 435 - 495 °F | |
| Middle Barrel Temperature | 235 - 268 °C | 455 - 515 °F | |
| Front Barrel Temperature | 246 - 279 °C | 475 - 535 °F | |
| Melt Temperature | 249 - 277 °C | 480 - 530 °F | |
| Mold Temperature | 51.7 - 85.0 °C | 125 - 185 °F | |
| Drying Temperature | 76.7 - 82.2 °C | 170 - 180 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |