RedEye On Demand VeroBlack PolyJet™ FC870 for Rapid Prototyping

Category Polymer , Rapid Prototyping Polymer , Thermoplastic
Manufacturer RedEye On Demand
Trade Name VeroBlack PolyJet™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RedEye On Demand VeroBlack PolyJet™ FC870 for Rapid Prototyping.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vero PolyJet Resin (VeroBlue™ FC840 & VeroBlack™ FC870) is a photopolymer resin designed for precise jetting in super fine layers by PolyJet™ Technology, often used in rapid prototyping. Our Vero PolyJet Resin materials offer great surface finish with improved mechanical properties as compared to our Clear PolyJet Resin (FC720). These parts are built at a layer thickness of 16 microns (0.0006 inch or 0.01524mm) and can produce parts with fine feature detail.ApplicationsVero PolyJet Resins work well for prototypes that require smooth surface finish and high feature detail. These resins offer improvements as compared to our Clear PolyJet Resin such as improved mechanical properties, enhanced visualization of details and edges, improved humidity resistance and better flexural strength. Parts from this material can be chrome plated or used as a master for silicone molds. Typical industries included toys, foot wear, architecture and any industry where feature detail and surface finish our required.
Mechanical Properties Metric English Comments
Hardness, Rockwell M 81
81
Hardness, Shore D 83
83
Tensile Strength, Yield 49.9 MPa
7240 psi
ASTM D638
Elongation at Break 15 - 25 %
15 - 25 %
ASTM D638
Tensile Modulus 2.495 GPa
361.9 ksi
ASTM D638
Flexural Yield Strength 74.6 MPa
10800 psi
ASTM D790
Flexural Modulus 2.137 GPa
310.0 ksi
ASTM D790
Izod Impact, Notched 0.375 J/cm
0.703 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 49.0 °C
120 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 45.0 °C
113 °F
ASTM D648
Glass Transition Temp, Tg 58.0 °C
136 °F
DMA (SYSS)