Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 120 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	48.8 °C	120 °F	ASTM D648-06
Objet FullCure® 840 Vero Blue Resin for Rapid Prototyping Information provided by American Precision Prototyping, LLC
Deflection Temperature at 0.46 MPa (66 psi)	49.0 - 53.0 °C	120 - 127 °F	ASTM D648
Proto3000 Accura® 50 Plastic Stereolithography (SLA) Prototyping Polymer Simulate the properties and appearance of molded ABS with this durable, accurate and versatile plastic.Features:Durable and stiffOutstanding accuracy w/out shrinkage related distortionChoice of grey..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
RedEye On Demand VeroBlack PolyJet™ FC870 for Rapid Prototyping Vero PolyJet Resin (VeroBlue™ FC840 & VeroBlack™ FC870) is a photopolymer resin designed for precise jetting in super fine layers by PolyJet™ Technology, often used in rapid prototyping. Our Vero..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
RedEye On Demand VeroBlue PolyJet™ FC840 for Rapid Prototyping Vero PolyJet Resin (VeroBlue™ FC840 & VeroBlack™ FC870) is a photopolymer resin designed for precise jetting in super fine layers by PolyJet™ Technology, often used in rapid prototyping. Our Vero..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
RedEye On Demand VeroWhite PolyJet Resin White for Rapid Prototyping Vero PolyJet Resin (VeroBlue™ FC840 & VeroBlack™ FC870) is a photopolymer resin designed for precise jetting in super fine layers by PolyJet™ Technology, often used in rapid prototyping. Our Vero..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
ExxonMobil Escorene® LL-8361 LLDPE, Rotational Molding Powder (discontinued **) Data Provided by Exxon Chemical Canada.Characteristics: Fully formulated, UV-8 type protection, Good flowUses: Consumer items, Potable water tanks, Laundry tubs
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
NOVA Chemicals Novapol® TR-0338-UI Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, ..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
NOVA Chemicals Novapol® TR-0338-UIG Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, ..
Deflection Temperature at 0.46 MPa (66 psi)	48.9 - 65.6 °C	120 - 150 °F	ASTM D648
Arkema Group Kynar Flex® 2950 PVDF Copolymer (discontinued **) Copolymer Series, Kynar® components are used extensively in the high purity semiconductor market, the pulp and paper industry, nuclear waste processing, and the general chemical processing industry..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
Covestro Baydur® SFR-243 Polyurethane Composite RRIM Foam, 15% Milled Glass Filled, MDI-based 2-Component Liquid System 0.25 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – C..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 - 53.0 °C	120 - 127 °F	ASTM D648
3D Systems Accura® 50 Plastic for SLA® Systems Simulate the properties and appearance of molded ABS. For use with the Viper™ SLA® system, SLA 3500, SLA 5000 and SLA 7000 systems.ApplicationsFunctional components for assemblies, mock-ups and te..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 - 65.0 °C	120 - 149 °F	ASTM D648
Arkema Group KYNAR FLEX® 2950-05 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Very flexible, flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toug..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM-D648
Braskem IJ33D LLDPE Injection Molding Polyethylene Copolymer IJ33D is a linear low-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high fluidity, excellent flexibi..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM-D648
Braskem IN34 LLDPE Injection Molding Polyethylene Copolymer IN34 is a linear low-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high fluidity, excellent flexibil..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 - 62.0 °C	120 - 144 °F	Average value: 56.1 °C Grade Count:36
Overview of materials for Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade". Each property range of values report..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 - 60.0 °C	120 - 140 °F	Average value: 54.4 °C Grade Count:13
Overview of materials for Linear Medium Density Polyethylene (LMDPE), Rotational Molded This property data is a summary of similar materials in the MatWeb database for the category "Linear Medium Density Polyethylene (LMDPE), Rotational Molded". Each property range of values reported i..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
ExxonMobil Escorene® LL-8302 LMDPE Rotational Molding Grade (discontinued **) Data provided by the manufacturer, Exxon Chemical.LL-8300 series are linear medium density polyethylene resins that provide outstanding environmental stress crack resistance. LL-8302 is the base re..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 °C	120 °F	ASTM D648
ExxonMobil Escorene® LL-8361 LMDPE Rotational Molding Grade (discontinued **) Data provided by the manufacturer, Exxon Chemical.LL-8300 series are linear medium density polyethylene resins that provide outstanding environmental stress crack resistance. LL-8361 is fully formu..
Deflection Temperature at 0.46 MPa (66 psi)	49.0 - 65.0 °C	120 - 149 °F	ASTM D648
Arkema Group KYNAR FLEX® 2750-01 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Very flexible, lubricated. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani..