Rogers Corporation Poron® Shock Seal™ 4790-79-9 Handheld Urethane Foam, Handheld Grade, PET Reinforced

Category Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane Foam, Unreinforced
Manufacturer Rogers Corporation
Trade Name Poron® Shock Seal™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation Poron® Shock Seal™ 4790-79-9 Handheld Urethane Foam, Handheld Grade, PET Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Extreme Impact Protection, Ultimate ReliabilitySpecifically engineered to protect sensitive components from damage caused by impactConsistent cushioning performance through repeated impactsExcellent compression set resistanceSupporting Material - Clear Polyester FilmInformation provided by Rogers Corporation.
Physical Properties Metric English Comments
Density 0.144 g/cc
0.00521 lb/in³
ASTM D3574-95 Test A
1.395 g/cc
0.05040 lb/in³
supporting material; ASTM D1505
Thickness 533 - 991 microns
21.0 - 39.0 mil
Range of Thicknesses Available
Mechanical Properties Metric English Comments
Tensile Strength, Yield 103 MPa
15000 psi
F5, supporting material; ASTM D882
Elongation at Break 150 %
150 %
supporting material; ASTM D882
Tensile Modulus 3.45 GPa
500 ksi
MD, supporting material; ASTM D882
Compressive Yield Strength 0.0138 MPa

@Strain 25.0 %
2.00 psi

@Strain 25.0 %
0.2"/min. strain rate
Coefficient of Friction, Dynamic 0.40
0.40
A/B, supporting material; ASTM D1894
Compression Set <= 5.0 %

@Temperature 23.0 °C
<= 5.0 %

@Temperature 73.4 °F
ASTM D1667-90 Test D
<= 10 %

@Temperature 70.0 °C
<= 10 %

@Temperature 158 °F
ASTM D3574-95 Test D
Film Tensile Strength at Break, MD 207 MPa
30000 psi
supporting material; ASTM D882
Thermal Properties Metric English Comments
Shrinkage, MD 1.2 %

@Temperature 150 °C,
Time 2340 sec
1.2 %

@Temperature 302 °F,
Time 0.650 hour
supporting material
Shrinkage, TD 0.00 %

@Temperature 150 °C,
Time 2340 sec
0.00 %

@Temperature 302 °F,
Time 0.650 hour
supporting material