SABIC Innovative Plastics LNP STAT-LOY 93000LTH Acrylic

Category Polymer , Thermoplastic , Acrylic (PMMA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Stat-loy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-LOY 93000LTH Acrylic.pdf
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-LOY* 93000LTH is a compound based on Acrylic resin. Added features of this material include: Antistatic, Transparent and Formulation Locked.
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 7.0 %
7.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 1.78 GPa
258 ksi
5 mm/min; ASTM D638
Flexural Strength 47.0 MPa
6820 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.47 GPa
213 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.400 J/cm
0.749 ft-lb/in
Izod Impact, Unnotched 6.67 J/cm
12.5 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 66.0 °C

@Thickness 3.20 mm
151 °F

@Thickness 0.126 in
unannealed; ASTM D648
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+9 - 1.00e+11 ohm-cm
1.00e+9 - 1.00e+11 ohm-cm
Surface Resistance 1.00e+9 - 1.00e+11 ohm
1.00e+9 - 1.00e+11 ohm
Static Decay <= 1.0 sec
<= 1.0 sec
5000V to <50V; FTMS101B