SABIC Innovative Plastics LNP THERMOCOMP PX85100 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PX85100 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* PX85100 is a compound based on Nylon 6 resin containing Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 156 MPa | 22600 psi | Type I, 5 mm/min; ASTM D638 |
| 156 MPa | 22600 psi | ASTM D638 | |
| Elongation at Break | 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 |
| 2.7 % | 2.7 % | ASTM D638 | |
| Elongation at Yield | 9.0 % | 9.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 10.34 GPa | 1500 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
| Flexural Modulus | 8.02 GPa | 1160 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.02 GPa | 1160 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.73 J/cm | 20.10 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |