Polymer Property : Tensile Modulus = 10.34 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC LNP* LUBRICOMP* DFL369XF is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Flame Retardant.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU (Asia Pacific) LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 LNP* LUBRICOMP* RFL36L is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 (Asia Pacific) LNP* Lubricomp* RFL36L is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RX06480 PA 66 (Asia Pacific) LNP* LUBRICOMP* RX06480 is a compound based on Nylon 66 resin containing PTFE, Glass Fiber, Silicone. Added features of this material include: Internally Lubricated.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT LNP LUBRICOMP* WFL36 is a compound based on PBT resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT (Asia Pacific) LNP LUBRICOMP* WFL36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Modulus	10.34 GPa	1500 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DE002 PC LNP* STAT-KON* DE002 is a Polycarbonate base resin containing 10% Carbon Fiber. Added feature of this grade is: Electrically Conductive.
Tensile Modulus	10.34 GPa	1500 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DE002 PC (Asia Pacific) LNP* Stat-Kon* DE002 is a Polycarbonate containing Carbon Fiber.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DEL339XF PC LNP* STAT-KON* DEL339XF is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 15% PTFE. Added features include: Electrically Conductive, Flame Retardant, Wear Resistant.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp DF008P PC LNP THERMOCOMP* DF008P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the ..
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12 LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12 (Asia Pacific) LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PX85100 PA 6 LNP* THERMOCOMP* PX85100 is a compound based on Nylon 6 resin containing Proprietary Filler(s).
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DEL339XF PC (Asia Pacific) LNP* Stat-kon* DEL339XF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant,..
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp DF008P PC (Asia Pacific) LNP* THERMOCOMP* DF008P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the..
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP EF006H PEI LNP* Thermocomp* EF006H is a compound based on Polyetherimide resin containing 30% Glass Fiber. Added features include: Healthcare.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP EF006H PEI (Asia Pacific) LNP* Thermocomp* EF006H is a compound based on Polyetherimide resin containing Glass Fiber.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC (Asia Pacific) LNP* Lubricomp* DFL369XF is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant.
Tensile Modulus	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractible.