ScanTube FEP Tubing
| Category | Polymer , Thermoplastic , Fluoropolymer , FEP , Fluorinated Ethylene Propylene (FEP), Molded/Extruded |
| Manufacturer | ScanTube |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ScanTube FEP Tubing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by ScanTube, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.15 g/cc | 0.0777 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.010 % | <= 0.010 % | ASTM D257 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength | 24.1 MPa | 3500 psi | ASTM D638, ASTM D1708 |
| Elongation at Break | 300 % | 300 % | ASTM D638, ASTM D1708 |
| Tensile Modulus | 0.345 GPa | 50.0 ksi | ASTM D638 |
| Flexural Modulus | 0.655 GPa | 95.0 ksi | ASTM D790 |
| Compressive Strength | 15.2 MPa | 2200 psi | ASTM D695 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.202 W/m-K | 1.40 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 270 °C | 518 °F | |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Continuous |
| Deflection Temperature at 0.46 MPa (66 psi) | 59.0 °C | 138 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | >= 95 % | >= 95 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.1 @Frequency 1000 Hz |
2.1 @Frequency 1000 Hz |
ASTM D150 |
| 2.1 @Frequency 1.00e+6 Hz |
2.1 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 78.7 kV/mm | 2000 kV/in | Short Term; 10 mil film; ASTM D149 |
| Dissipation Factor | 0.00010 @Frequency 1000 Hz |
0.00010 @Frequency 1000 Hz |
ASTM D150 |
| 0.00080 @Frequency 1.00e+6 Hz |
0.00080 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Resistance | Excellent | |
| Weather Resistance | Excellent |
Users viewing this material also viewed the following:
- Omni Plastics OmniTech™ PA6/6 GR15 MS2 Wear-and-Friction Molybdenum Disulfide filled Nylon
- Omya HYDROCARB® 95 HS Calcium Carbonate
- SABIC Innovative Plastics Lexan® EXL1810T PC Copolymer (Europe-Africa-Middle East)
- Ineos ABS Lustran® 356 Extrusion, Low-Gloss (discontinued **)
- Kinlead PL11 Lamination Grade BOPP Plain Film (thickness: 18 µm)
- DuPont Conpol™ 20S1 Ethylene-Methacrylic Acid Additive Resin
- Weartech International WT-595 Iron Hardfacing & Wear Resistant Alloy
- Epoxy Technology EPO-TEK® T7109-18 Electrically Insulating Epoxy Paste
- Arlon CP-499CA Bulk Compound
- Akzo Nobel Trigonox® EHP-C65 Polymerization Initiator
Copyright © lookpolymers.com All Rights Reserved