Sharadaa Ceramics REFCAST LC60ABR Low Cement Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics REFCAST LC60ABR Low Cement Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: We bring to our clients a range of Low Cement Castables, that are available in varied alumina content and service range. Designed for abrasion resistance application, these are widely used in furnaces such as ladle back up lining, sintering furnace roof and soaking pit covers.Information provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | >= 2.35 g/cc | >= 0.0849 lb/in³ | Dried at 110°C |
| Grain Size | <= 10000 µm | <= 10000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0118 GPa @Temperature 110 °C |
1.71 ksi @Temperature 230 °F |
|
| 0.0147 GPa @Temperature 1100 °C |
2.13 ksi @Temperature 2010 °F |
||
| 0.0177 GPa @Temperature 1500 °C |
2.57 ksi @Temperature 2730 °F |
||
| Compressive Strength | 88.3 MPa @Temperature 110 °C |
12800 psi @Temperature 230 °F |
Cold Crushing |
| 98.1 MPa @Temperature 1100 °C |
14200 psi @Temperature 2010 °F |
Cold Crushing | |
| 108 MPa @Temperature 1500 °C |
15600 psi @Temperature 2730 °F |
Cold Crushing | |
| 24.5 MPa @Time 86400 sec |
3560 psi @Time 24.0 hour |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.05 W/m-K @Temperature 400 °C, Time 10800 sec |
7.29 BTU-in/hr-ft²-°F @Temperature 752 °F, Time 3.00 hour |
|
| 1.16 W/m-K @Temperature 600 °C, Time 10800 sec |
8.05 BTU-in/hr-ft²-°F @Temperature 1110 °F, Time 3.00 hour |
||
| 1.28 W/m-K @Temperature 800 °C, Time 10800 sec |
8.88 BTU-in/hr-ft²-°F @Temperature 1470 °F, Time 3.00 hour |
||
| Maximum Service Temperature, Air | 1600 °C | 2910 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | >= 60 % | >= 60 % | |
| Fe2O3 | <= 1.6 % | <= 1.6 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | -0.1 - 0.1% | 800°C |
| -0.3 - 0.3% | 1100°C | |
| -1.0 -1.0% | 1500°C | |
| Refractoriness | >1804°C | |
| Thermal Expansion | 0.3 | 1000°C, Reversible |
| Water Required to Mix | 4 - 5% |
Users viewing this material also viewed the following:
- Quadrant EPP Nylatron® GS Nylon, Extruded MoS2 Filled Type 66 (ASTM Product Data Sheet)
- SABIC Innovative Plastics LNP LUBRICOMP DBP32EI PC (Asia Pacific)
- KB Alloys 10% Bismuth Aluminum Alloy
- A. Schulman POLYTROPE™ CB 1010U-330 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- Trelleborg AEM Syntac® 350 Syntactic Foam
- ConocoPhillips SynXPA® 100 R&O Oil
- Hippe UP GM 202 Woven Glass Mat Reinforced Polyester (unsaturated) Resin - Sheet
- Dow HDPE 12450N High Density Polyethylene
- Bhansali Engineering Abstron KU603 ABS Heat Resistant
- CENTROPLAST CENTROLEN PP GF 30 Polypropylene 30% glass fiber
Copyright © lookpolymers.com All Rights Reserved