Styron EMERGEâ„¢ 4410-11 MFR Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name EMERGE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron EMERGEâ„¢ 4410-11 MFR Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EMERGEâ„¢ PC 4410-11 advanced resin is a high impact polycarbonate resin designed for Information Technology Equipment and Injection Molding Applications.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
ASTM D955
Melt Flow 11 g/10 min

@Load 1.20 kg,
Temperature 300 °C
11 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.8 MPa
8100 psi
0.125 in, injection molded, unannealed; ASTM D638
Elongation at Break 130 %
130 %
0.125 in, injection molded, unannealed; ASTM D638
Flexural Strength 89.6 MPa
13000 psi
0.125 in, injection molded, unannealed; ASTM D790
Flexural Modulus 2.28 GPa
330 ksi
0.125 in, injection molded, unannealed; ASTM D790
Izod Impact, Notched 5.34 J/cm
10.0 ft-lb/in
-22°F; ASTM D256
6.94 J/cm
13.0 ft-lb/in
73°F; ASTM D256
Dart Drop, Total Energy 57.0 J
42.0 ft-lb
0.125 in, 8000 ipm; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
0.125 in, 8000 ipm, unannealed; ASTM D648
136 °C
277 °F
0.125 in, 8000 ipm, annealed; ASTM D648
Vicat Softening Point 146 °C
295 °F
50°C/hr, 50N; ASTM D1525
UL RTI, Electrical 110 °C
230 °F
UL 746
UL RTI, Mechanical with Impact 95.0 °C
203 °F
UL 746
UL RTI, Mechanical without Impact 105 °C
221 °F
UL 746
Flammability, UL94 HB
HB
0.0625 in