- Techmer ES Luriblend® PES GF30 TL15 30% Glass Filled
Techmer ES Luriblend® PES GF30 TL15 30% Glass Filled
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 30%Glass Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PES GF30 TL15 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%)Features: LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % @Time 86400 sec |
0.30 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm @Thickness 3.17 mm |
0.0015 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 125 MPa | 18200 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 172 MPa | 25000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 3.17 mm |
1.60 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm @Thickness 3.17 mm |
7.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.26 | 0.26 | ASTM D1894 |
| Coefficient of Friction, Static | 0.20 | 0.20 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1105-8135/VI PEEK, unreinforced, easy flowing
- Kingfa PA66-RG301 Flame Retardant, 30% Glass Fiber Reinforced PA66
- Gouda Vuurvast VIBRON 180 Dense Vibrating Refractory Castable
- Techmer ES HiFill FR® PC FR HS GY154
- Lubrizol ESTANE® GP92AT Ether Based Thermoplastic Polyurethane
- Dow SE BCP 817 Stereospecific high cis-1,4 Polybutadiene (BR)
- Ametek P409L P/M Stainless Steel, Sintered from 6.45 g/cc Green Density
- Cheng Yu Plastic A703G25 ABS 25% Glass Fiber Reinforced
- Lubrizol Advanced Materials Pearlstick® 45-40/03 Polycaprolactone based TPU (discontinued **)
Copyright © lookpolymers.com All Rights Reserved