- Tipco Tipcofil® AM 300 - 15% Mineral Reinforced Nylon-6 Compound, with High Heat Stability
Tipco Tipcofil® AM 300 - 15% Mineral Reinforced Nylon-6 Compound, with High Heat Stability
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Tipco Industries Ltd., India |
| Trade Name | Tipcofil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tipco Tipcofil® AM 300 - 15% Mineral Reinforced Nylon-6 Compound, with High Heat Stability.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Mineral Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Water Absorption | 1.4 % | 1.4 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min | 14 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | ASTM D638 |
| Elongation at Break | >= 25 % | >= 25 % | ASTM D638 |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | ASTM D790 |
| Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 240 °C | 464 °F | |
| Rear Barrel Temperature | 235 °C | 455 °F | |
| Middle Barrel Temperature | 245 °C | 473 °F | |
| Front Barrel Temperature | 255 °C | 491 °F | |
| Nozzle Temperature | 245 °C | 473 °F | |
| Mold Temperature | 85.0 °C | 185 °F | |
| Drying Temperature | 80.0 °C | 176 °F |
Users viewing this material also viewed the following:
- Osprey Metals 430L Stainless Steel Powder (Grade 80% - 22)
- Arkema Group Oroglas® DRM Acrylic, Extrusion Grade (discontinued **)
- Magyar Aluminum ALO-G2-2 Alumina
- Kolon Kopa® KN153G30 Nylon 6 Resin
- SABIC Innovative Plastics LNP LUBRICOMP QFN16 PA 6/10
- UBE 5034T Nylon 6/66 Monofilament (Drawing Ratio=4.5)
- Lubrizol Estane® ALR E87A Thermoplastic Polyurethane
- Beijing Chemical Industry KAIFA® 301-G10 PBT Resin
- Beijing Ranger Chem SM-E-39D Semi Solid Epoxy Resin
- Aremco Corr-Paint™ CP4090-S1 High Temperature Protective Coating, Silicone
Copyright © lookpolymers.com All Rights Reserved