Total PPH 4026 Polypropylene Homopolymer, Film

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Total Atofina
Trade Name PPH
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPH 4026 Polypropylene Homopolymer, Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene PPH 4026 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min for the cast extrusion of films with outstanding stiffness and heat resistance.Polypropylene PPH 4026 is intended for applications like hot fill food packaging, labeling, twist or lamination films.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.905 g/cc
0.905 g/cc
ISO 1183
Bulk Density 0.525 g/cc
0.0190 lb/in³
ISO 1183
Thickness 50.0 microns
1.97 mil
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 95
95
ISO 2039-2
Film Tensile Strength at Yield, MD 31.0 MPa
4500 psi
ISO 527-3
Film Tensile Strength at Yield, TD 29.0 MPa
4210 psi
ISO 527-3
Tensile Strength, Yield 39.0 MPa
5660 psi
ISO 527-2
Film Elongation at Break, MD 470 %
470 %
ISO 527-3
Film Elongation at Break, TD 580 %
580 %
ISO 527-3
Elongation at Yield 9.0 %
9.0 %
ISO 527-2
Tensile Modulus 2.05 GPa
297 ksi
ISO 527-2
Flexural Modulus 2.00 GPa
290 ksi
ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO 180
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179
Elmendorf Tear Strength, MD 0.600 g/micron
15.2 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 9.00 g/micron
229 g/mil
ISO 6383-2
Dart Drop Test 80.0 g
0.176 lb
ISO 7765-1
Film Tensile Strength at Break, MD 62.0 MPa
8990 psi
ISO 527-3
Film Tensile Strength at Break, TD 35.0 MPa
5080 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
120°C per hour; ISO 752
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
120°C per hour; ISO 752
Vicat Softening Point 97.0 °C

@Load 5.10 kg
207 °F

@Load 11.2 lb
50°C per hour; ISO 306
153 °C

@Load 1.02 kg
307 °F

@Load 2.25 lb
50°C per hour; ISO 306
Optical Properties Metric English Comments
Haze 14 %
14 %
ISO 14782
Gloss 51 %
51 %
at 45°; ASTM D2457