Zotefoams Plastazote® LD70 Low Density Polyethylene Foam

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Zotefoams
Trade Name Plastazote®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Plastazote® LD70 Low Density Polyethylene Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0600 - 0.0760 g/cc
0.00217 - 0.00275 lb/in³
sheet density
0.0700 g/cc
0.00253 lb/in³
Nominal skin/skin; BS ISO 7214 1998
Cell Length 0.600 mm
0.0236 in
Typical Diameter
0.350 - 0.900 mm
0.0138 - 0.0354 in
Mechanical Properties Metric English Comments
Hardness, Shore OO 74
74
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 0.740 MPa
107 psi
ISO 7214 1998
Elongation at Break 165 %
165 %
Flexural Modulus 0.00270 GPa
0.392 ksi
BS4370, part 4, method 14
Compressive Yield Strength 0.146 MPa

@Strain 10.0 %
21.2 psi

@Strain 10.0 %
BS ISO 7214 1998
0.158 MPa

@Strain 25.0 %
22.9 psi

@Strain 25.0 %
BS ISO 7214 1998
0.198 MPa

@Strain 40.0 %
28.7 psi

@Strain 40.0 %
BS ISO 7214 1998
0.248 MPa

@Strain 50.0 %
36.0 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 2.075 kN/m
11.84 pli
BS EN ISO 8067 1995
Compression Set 2.0 %

@Time 79200 sec,
Strain 25.0 %
2.0 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
5.0 %

@Time 79200 sec,
Strain 25.0 %
5.0 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
6.0 %

@Time 79200 sec,
Strain 50.0 %
6.0 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
13 %

@Time 79200 sec,
Strain 50.0 %
13 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Thermal Conductivity 0.0500 W/m-K
0.347 BTU-in/hr-ft²-°F
mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air 105 °C
221 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 0.60

@Thickness 13.0 mm
0.60

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
1.0

@Thickness 5.00 mm
1.0

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
Shrinkage <= 1.0 %

@Temperature 80.0 °C
<= 1.0 %

@Temperature 176 °F
<= 2.0 %

@Temperature 90.0 °C
<= 2.0 %

@Temperature 194 °F