Zotefoams Plastazote® MP15FR Metallocene Polyethylene Foam, Flame Retardant

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Zotefoams
Trade Name Plastazote®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Plastazote® MP15FR Metallocene Polyethylene Foam, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact regulations.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0150 g/cc
0.000542 lb/in³
Nominal skin/skin; BS ISO 7214 1998
0.0140 - 0.0180 g/cc
0.000506 - 0.000650 lb/in³
sheet density
Cell Length 0.200 - 0.600 mm
0.00787 - 0.0236 in
0.900 mm
0.0354 in
Typical Diameter
Mechanical Properties Metric English Comments
Hardness, Shore OO 26
26
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 0.353 MPa
51.2 psi
ISO 7214 1998
Elongation at Break 146 %
146 %
Compressive Yield Strength 0.0180 MPa

@Strain 10.0 %
2.61 psi

@Strain 10.0 %
BS ISO 7214 1998
0.0350 MPa

@Strain 25.0 %
5.08 psi

@Strain 25.0 %
BS ISO 7214 1998
0.0620 MPa

@Strain 40.0 %
8.99 psi

@Strain 40.0 %
BS ISO 7214 1998
0.0890 MPa

@Strain 50.0 %
12.9 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 0.545 kN/m
3.11 pli
BS EN ISO 8067 1995
Compression Set 5.0 %

@Time 79200 sec,
Strain 25.0 %
5.0 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
18 %

@Time 79200 sec,
Strain 25.0 %
18 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
26.5 %

@Time 79200 sec,
Strain 50.0 %
26.5 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
38 %

@Time 79200 sec,
Strain 50.0 %
38 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Thermal Conductivity 0.0390 W/m-K
0.271 BTU-in/hr-ft²-°F
mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air 95.0 °C
203 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 2.6

@Thickness 13.0 mm
2.6

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
4.0

@Thickness 5.00 mm
4.0

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
Descriptive Properties Value Comments
Flammability Automotive: FMVSS.302 burn rate
Pass: > 3 mm thick
Aviation: CAA8/2-2.2b
Complies
Construction: DIN4102 B1
Pass: 6 to 20 mm thick