Polymer Property : Linear Mold Shrinkage, Flow = 0.010 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.010 - 0.012 cm/cm @Thickness 3.20 mm	0.010 - 0.012 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics EXTEM XH1015 TPI Resin Thermoplastic Polyimide Extem* XH1015 Resin.
Linear Mold Shrinkage, Flow	0.010 cm/cm @Time 86400 sec	0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DL0039E PC (Asia Pacific) LNP* Lubricomp* DL0039E is a compound based on Polycarbonate resin containing PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant, Easy Molding.
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in
Ineos ABS Triax® 1180 ABS + Polyamide Blend (Conditioned) (discontinued **) Key Features:UnfilledHigh impact or high impact modifiedSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business r..
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	ASTM D955
Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin. Th..
Linear Mold Shrinkage, Flow	0.010 - 0.012 cm/cm @Thickness 3.20 mm	0.010 - 0.012 in/in @Thickness 0.126 in	ASTM D955
LG Chemical LUPOL HI5204S PP+MF20%, High Impact Description: Injection Molding, PP+MF20%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 26221-73-8 and 14807-96-6Information provided by LG Chemical
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	ISO 294
Inno-Comp INNOPOLÂ® CS 1-3120 B DEL 20% Talc Filled Polypropylene Homopolymer INNOPOLÂ® CS 1-3120 B DEL is developed for producing injection molded automotive components.All information provided by INNO-COMP.
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	ISO 294
Inno-Comp INNOPOLÂ® CS 1-3120 N DEL 20% Talc Filled Polypropylene Homopolymer INNOPOLÂ® CS 1-3120 B DEL is developed for producing injection molded automotive components.All information provided by INNO-COMP.
Linear Mold Shrinkage, Flow	0.010 cm/cm @Thickness 3.17 mm	0.010 in/in @Thickness 0.125 in	1/8" Section
Lucent Polymers TPP-140 Polypropylene, Homopolymer, 40% Talc Filled Melt Flow Adjustable for ApplicationAdd "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in
Solvay TECHNYLÂ® A 548B2 V15 PA66, 15% glass fiber, DRY Description: TECHNYLÂ® A 548B2 V15 is a polyamide 6.6, reinforced with 15% of glass fiber, heat stabilized, impact modified, for blow molding. This product is available in black color.Benefits: Th..
Linear Mold Shrinkage, Flow	0.010 - 0.030 cm/cm @Time 86400 sec	0.010 - 0.030 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp ML002S PP LNP* Lubricomp* ML002S is a compound based on Polypropylene containing PTFE. Characteristics of this grade are: Heat Stabilized and Internally Lubricated.This data was supplied by SABIC-IP for the..
Linear Mold Shrinkage, Flow	0.010 - 0.017 cm/cm	0.010 - 0.017 in/in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WL004 is a compound based on Polybutylene Terephalate resin containing PTFE.
Linear Mold Shrinkage, Flow	0.010 - 0.020 cm/cm	0.010 - 0.020 in/in	on tensile bar; SABIC Method
SABIC Innovative Plastics ValoxÂ® VX7024 PBT (Europe-Africa-Middle East) VALOX VX7024 is a 12% mineral filled PBT injection moulding resin with excellent mechanical properties.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Linear Mold Shrinkage, Flow	0.010 - 0.012 cm/cm @Thickness 3.20 mm	0.010 - 0.012 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics XenoyÂ® 5720U PBT+PC Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	SABIC Method
SABIC Innovative Plastics LNP Thermocomp MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB..
Linear Mold Shrinkage, Flow	0.010 - 0.012 cm/cm	0.010 - 0.012 in/in	on tensile bar; SABIC Method
SABIC Innovative Plastics Noryl GTX GTX966 PPE+PA66 >PPE+PA66-I-TD10
Linear Mold Shrinkage, Flow	0.010 - 0.012 cm/cm @Thickness 3.20 mm	0.010 - 0.012 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics Noryl GTX GTX966 PPE+PA66 >PPE+PA66-I-TD10
Linear Mold Shrinkage, Flow	0.010 - 0.013 cm/cm @Thickness 3.20 mm	0.010 - 0.013 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics Noryl GTX GTX977 PPE+PA66 (Asia Pacific) Noryl GTX GTX977 resin is a mineral reinforced conductive Noryl GTX with a improved CTE (7) with a balanced performance of Impact and stiffness. (developmental grade : EXNX0074)This data was supplie..
Linear Mold Shrinkage, Flow	0.010 cm/cm @Thickness 3.17 mm	0.010 in/in @Thickness 0.125 in	ASTM D955
Techmer ES HiFill FRÂ® PA6 GF13 FR-N IM BK 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilize, Impact Modifier and LubricantFeatures: Flame Retardant, Heat S..
Linear Mold Shrinkage, Flow	0.010 cm/cm @Time 86400 sec	0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP MB006HS PP LNP* THERMOCOMP* MB006HS is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized, Healthcare.
Linear Mold Shrinkage, Flow	0.010 - 0.014 cm/cm	0.010 - 0.014 in/in	ASTM D955
Chase Plastics CP Pryme® N300HL (Dry) Nylon 6, Heat Stabilized, Lubricated, Recycled Content Features: Heat StabilizedLubricatedRecycled contentForm: PelletsInformation provided by Chase Plastics.
Linear Mold Shrinkage, Flow	0.010 - 0.014 cm/cm	0.010 - 0.014 in/in	DIS 294-4
Wellman Wellamid® FRGS25-66-NBK3 Nylon 66, 25% Glass Sphere Reinforced, Flame Retardant All information provided by Wellman Engineered Resins.
Linear Mold Shrinkage, Flow	0.010 cm/cm @Thickness 3.20 mm	0.010 in/in @Thickness 0.126 in
Unitika A1030SR PA6, Conditioned Information provided by Unitika Ltd.
Linear Mold Shrinkage, Flow	0.010 - 0.020 cm/cm	0.010 - 0.020 in/in	ASTM D955
Elastocon TPE Technologies Elastocon® 8078B Thermoplastic Elastomer Elastocon® 8078B is a black thermoplastic elastomer formulated for applications that require rubber-like properties and a good surface finish. Elastocon® 8078B is well suited for consumer goods a..
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	DAM; ISO 294-4 2577
DuPont Performance Polymers Zytel® HTN FE8200 BK431 Polyphthalamide (PPA) (Unverified Data**) Unreinforced Toughened PPA High Performance Polyamide Zytel HTNFE8200 BK431 is an unreinforced toughened heat stabilized lubricated high performance polyamide resin for injection molding. It is also..
Linear Mold Shrinkage, Flow	0.010 - 0.012 cm/cm	0.010 - 0.012 in/in	on Tensile Bar; ISO 294
Eurostar Staramide AST43 PA66, Impact Modified, Injection Molded AST43 is a Low Temperature Impact Modified Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	ASTM D955
Clariant Renol PA101L Nylon 66, General Purpose, Lubricated Data provided by Clariant Masterbatches
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	ASTM D955
Clariant Renol PA101LRD-190 Nylon 66, General Purpose, Lubricated Data provided by Clariant Masterbatches
Linear Mold Shrinkage, Flow	0.010 cm/cm @Thickness 3.20 mm	0.010 in/in @Thickness 0.126 in
Unitika EX-1020K PA6, Dry Conducting nylonInformation provided by Unitika Ltd.
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	ISO 294-4, 2577
EMS-Grivory Grivory® L 25A NZ PA12-I Product Description: Grilamid L 25A NZ is a high viscosity extrusion grade Polyamide 12 (PA12). Grilamid L 25A NZ is hydrolysis and heat stabilized and impact modified. The main features of Grilamid..