| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 78.2 MPa | 11300 psi | ASTM D790 |
| PolyOne Geon™ Vinyl Rigid Extrusion L1101 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Flexural Strength | 77.9 MPa | 11300 psi | ASTM D790 |
| PolyOne Geon™ Vinyl Rigid Extrusion L4857 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| Nilit FRIANYL B63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | <= 78.0 MPa | <= 11300 psi | ISO 178 |
| Polykemi AB POLYabs F20 UV4 ABS, UV-stabilized Information provided by Polykemi AB |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| LG Chemical LUCEL FW-715C Friction and Wear Resistant POM, Polymeric Wear Additive, CaCo3 Filled, Low Warpage, Antistatic LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Kolon KOCETAL® K300BK Black Colored Grade Acetal Resin Colored, general purpose injection molding grade. Applications: General injection molding products.Information provided by API-Kolon. |
|||
| Flexural Strength | 77.9 MPa | 11300 psi | ASTM D790 |
| KYDEX® 2200LT Thermoplastic Sheet for Mass Transit Applications Features:Meets flamespread and smoke development requirements listed in 49 CFR 238Excellent formability and fabrication characteristicsAllows for tight tolerance controlsExcellent resistance to graf.. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | 5 mm/min; ISO 178 |
| Gromax BTE30-DN00N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT LNP LUBRICOMP* WL004 is a compound based on PBT resin containing 20% PTFE. Added features of this material include: Wear Resistant. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| SABIC Innovative Plastics LNP Lubriloy D2000XXH PC LNP LUBRILOY* D2000XXH is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated, Healthcare.This data was supplied.. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® 357 PBT+PC PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics XYLEX HX8300HP PC+POLYESTER (Asia Pacific) Medium flow, Transparent PC/Polyester alloy. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant... |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP 67001XXH PBT+PC LNP* THERMOCOMP* 67001XXH is a compound based on PC + PBT resin containing proprietary antimicrobial additives. Designed for touch surfaces in patient critical healthcare applications. Added featu.. |
|||
| Flexural Strength | 77.9 MPa | 11300 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP MX92284 PP (Asia Pacific) LNP* Thermocomp* MX92284 is a compound based on Polypropylene resin containing Proprietary Filler(s). |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP NX11302 PC+ABS (Asia Pacific) This is a PC/ABS compound with colorable, good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications |
|||
| Flexural Strength | 77.9 MPa | 11300 psi | ASTM D790 |
| Saint-Gobain Meldin® 7211 Isostatically Molded Graphite and PTFE Filled Polyimide Finished parts and basic shapes made from 10% by weight PTFE and 15% by weight graphite filled polyimide material for applications requiring a very low coefficient of friction and self-lubricating p.. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| Styron PULSEâ„¢ 2100 LG PC/ABS Engineering Resin Overview: PULSE 2100LG Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can .. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL N1052P PPE+HIPS (Asia Pacific) PPE+PS 105deg.C FR V-2 |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| SABIC Innovative Plastics NORYL PX0844 PPE+PS PPE+PS blend. Unfilled. UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Unitika M1030E PA6, Conditioned Nano composite nylonInformation provided by Unitika Ltd. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| Denka MALECCA K-200 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
| Flexural Strength | 77.9 MPa | 11300 psi | ASTM D790 |
| Adell YS-10 PC Alloy |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | 23°C, 50% RH; ASTM D790 |
| Asahi Kasei Xyron® 240Z Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| A. Schulman ComAlloy Hiloy® 422 Heavy Mineral Reinforced, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.40% Heavy Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | GB/9341 |
| Zhejiang Juner PC/PBT Alloy Applications: Shell of Small Household Electric Appliance, Auto Electric Appliance PartsInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | GB/9341 |
| Zhejiang Juner PC/PET Alloy Applications: Shell of Small Household Electric Appliance, Auto Electric Appliance PartsInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | 23°C, 50% RH; ASTM D790 |
| Asahi Kasei Xyron® A0501 PPE/PA AutomotiveInformation provided by Asahi Kasei |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC (Asia Pacific) LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing Glass Bead, PTFE, Flame Retardant. Added features of this material include:LNP* Lubricomp* DBL349E is a compound based .. |
|||
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL EX130 PPE+HIPS (Asia Pacific) PPE+PS Auto Exterior Grade |
|||