Styron PULSEâ„¢ 2100 LG PC/ABS Engineering Resin

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Styron
Trade Name PULSE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron PULSEâ„¢ 2100 LG PC/ABS Engineering Resin.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Overview: PULSE 2100LG Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can withstand high and low temperature extremes and rapid, repeated temperature fluctuations.Benefits:Low gloss appearance-20°F DuctilityWide range of performanceSuperior processabilityLot to lot consistencyGood chemical resistanceInformation provided by Styron
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ASTM D792; ISO 1183/B
Water Absorption 0.15 %

@Temperature 23.0 °C,
Time 86400 sec
 0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570; ISO 62
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
ASTM D955
0.0060 cm/cm
0.0060 in/in
ISO 294-4
Melt Flow 4.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 4.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
4.5 g/10 min

@Load 3.80 kg,
Temperature 260 °C
 4.5 g/10 min

@Load 8.38 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.8 MPa

@Thickness 3.20 mm
 7800 psi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Tensile Strength, Yield 51.0 MPa
7400 psi
ISO 527-2
53.1 MPa

@Thickness 3.20 mm
 7700 psi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Elongation at Break 120 %
120 %
ISO 527-2
130 %

@Thickness 3.20 mm
 130 %

@Thickness 0.126 in
 Injection Molded; ASTM D638
Elongation at Yield 4.5 %
4.5 %
ISO 527-2
5.0 %

@Thickness 3.20 mm
 5.0 %

@Thickness 0.126 in
 Injection Molded; ASTM D638
Tensile Modulus 2.50 GPa
363 ksi
ISO 527-2
2.34 GPa

@Thickness 3.20 mm
 339 ksi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Flexural Strength 78.0 MPa
11300 psi
ISO 178
80.7 MPa

@Thickness 3.20 mm
 11700 psi

@Thickness 0.126 in
 Injection Molded; ASTM D790
Flexural Modulus 2.30 GPa
334 ksi
ISO 178
2.34 GPa

@Thickness 3.20 mm
 339 ksi

@Thickness 0.126 in
 Injection Molded; ASTM D790
Izod Impact, Notched 5.30 J/cm

@Thickness 3.20 mm,
Temperature -29.0 °C
 9.93 ft-lb/in

@Thickness 0.126 in,
Temperature -20.2 °F
 Injection Molded; ASTM D256
6.40 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 12.0 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 Injection Molded; ASTM D256
Izod Impact, Notched (ISO) 24.0 kJ/m²

@Temperature -40.0 °C
 11.4 ft-lb/in²

@Temperature -40.0 °F
 ISO 180
32.0 kJ/m²

@Temperature -30.0 °C
 15.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 180
52.0 kJ/m²

@Temperature 23.0 °C
 24.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 180
Dart Drop, Total Energy 56.5 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 41.7 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 6.6 m/sec; ASTM D3763
62.1 J

@Thickness 3.20 mm,
Temperature -29.0 °C
 45.8 ft-lb

@Thickness 0.126 in,
Temperature -20.2 °F
 6.6 m/sec; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 74.0 µm/m-°C

@Temperature -40.0 - 82.0 °C
 41.1 µin/in-°F

@Temperature -40.0 - 180 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 128 °C

@Thickness 3.20 mm
 262 °F

@Thickness 0.126 in
 Unannealed; ISO 75-2/B
129 °C

@Thickness 3.20 mm
 264 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 106 °C

@Thickness 3.20 mm
 223 °F

@Thickness 0.126 in
 Unannealed; ISO 75-2/A
107 °C

@Thickness 3.20 mm
 225 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
Vicat Softening Point 128 °C
262 °F
ISO 306/B50
142 °C
288 °F
ISO 306/A120
143 °C

@Load 5.10 kg
 289 °F

@Load 11.2 lb
 Rate A (50°C/h); ASTM D1525
Optical Properties Metric English Comments
Gloss 25 %
25 %
Gardner, 60°, Smooth; ASTM D542
Descriptive Properties Value Comments
GMCP88 - Light Stipple 0.065
ASTM D524
Monticello 0.033
ASTM D524