Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PX0844 PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
PPE+PS blend. Unfilled. UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 13.7 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 13.7 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114
114
ASTM D785
Tensile Strength at Break 43.0 MPa
6240 psi
ISO 527
44.0 MPa
6380 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 47.0 MPa
6820 psi
ISO 527
49.0 MPa
7110 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 27 %
27 %
Type I, 50 mm/min; ASTM D638
43 %
43 %
ISO 527
Elongation at Yield 2.9 %
2.9 %
ISO 527
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.29 GPa
332 ksi
5 mm/min; ASTM D638
2.35 GPa
341 ksi
1 mm/min; ISO 527
Flexural Strength 78.0 MPa
11300 psi
ISO 178
Flexural Yield Strength 75.0 MPa
10900 psi
2.6 mm/min, 100 mm span; ASTM D790
80.0 MPa
11600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.24 GPa
325 ksi
2.6 mm/min, 100 mm span; ASTM D790
2.40 GPa
348 ksi
ISO 178
2.55 GPa
370 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.34 J/cm
4.38 ft-lb/in
ASTM D256
1.33 J/cm

@Temperature -40.0 °C
 2.49 ft-lb/in

@Temperature -40.0 °F
 ASTM D256
1.75 J/cm

@Temperature -30.0 °C
 3.28 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 17.0 kJ/m²
8.09 ft-lb/in²
80*10*4; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.70 J/cm²
8.09 ft-lb/in²
ISO 179/2C
1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Dart Drop, Total Energy 40.0 J

@Temperature 23.0 °C
 29.5 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 73.8 µm/m-°C

@Temperature 0.000 - 100 °C
 41.0 µin/in-°F

@Temperature 32.0 - 212 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 122 °C
252 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
120 °C

@Thickness 3.20 mm
 248 °F

@Thickness 0.126 in
 unannealed; ASTM D648
121 °C

@Thickness 6.40 mm
 250 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
105 °C

@Thickness 3.20 mm
 221 °F

@Thickness 0.126 in
 unannealed; ASTM D648
112 °C

@Thickness 6.40 mm
 234 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 125 °C
257 °F
Rate B/50; ISO 306
128 °C
262 °F
Rate B/120; ISO 306