Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | |
Prodways PLASTCure Cast 200 3D Printing Polymer Good reactivity and low viscosity. Outstanding burnout properties with nearly zero ash content.Highly suitable for direct investment casting or dental applications.Information provided by Genistar. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790-03 |
Proto3000 Objet Digital Materials™ DM_7210 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide .. |
|||
Flexural Strength | 60.0 - 90.0 MPa | 8700 - 13100 psi | Compression; ISO 178 |
Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve.. |
|||
Flexural Strength | 70.0 - 90.0 MPa | 10200 - 13100 psi | Compression; ISO 178 |
Raschig Group AMPLA® 7250 melamine-modified polyester Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow.. |
|||
Flexural Strength | 70.0 - 90.0 MPa | 10200 - 13100 psi | Compression; ISO 178 |
Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta.. |
|||
Flexural Strength | 70.0 - 90.0 MPa | 10200 - 13100 psi | Compression; ISO 178 |
Raschig Group DECAL® 5431 Phenolic Organically and inorganically filled phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax CCP PBT 1100-211X Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1100-211D Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1100-211H Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1100-211L Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1100-211M Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1100-211S Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Loxim 500 00HB Polycarbonate/Acrylonitrile Butadiene Styrene Information provided by Loxim Industries |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Loxim 500 00V0 Polycarbonate/Acrylonitrile Butadiene Styrene Information provided by Loxim Industries |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1100-211XG Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1200-211L Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 70.0 - 90.0 MPa | 10200 - 13100 psi | At Rupture; ISO 178 |
Vyncolit 3640 CG Novolac Phenolic Graphite filled phenolic molding compound with excellent dimensional stability. Self-lubricating and has a low coefficient of friction. Not suitable for electrical applications.USES: Gas meter par.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax CCP PBT 1200-211E Product Description: PBT unreinforced middle viscosity injection molding grade.Characteristics:Excellent electrical propertyExcellent temperature resistance, high heat distortion temperature.Excelle.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1100-211MB Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1200-211D Product Description: PBT unreinforced middle viscosity injection molding grade.Characteristics:Excellent electrical propertyExcellent temperature resistance, high heat distortion temperature.Excelle.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1200-211M Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |