Polymer Property : Tensile Strength at Break = 1310 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	9.03 MPa @Temperature 23.0 °C	1310 psi @Temperature 73.4 °F	Die C2 hr; ASTM D412
PolyOne Versaflex™ FFC 2882-87 Thermoplastic Elastomer (TPE) Versaflex™ FFC 2882-87 is designed to pass several fatty food extraction conditions identified in EU Directive 2002/72/EC, FDA 21 CFR 177.2600, and GB 4806.1-94. Versaflex™ FFC 2882-87 will also o..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D412
Polimeri Europa Europrene® SOL T 172 Styrene - Butadiene Block Copolymer Europrene® SOL T 172 is a radial block copolymer obtained by anionic polymerization. The polymer is based on styrene and butadiene, where bound styrene is 30% weight. The polymer is extended with..
Tensile Strength at Break	9.00 MPa	1310 psi	500 mm/min; ASTM D638
Eastman E6838-913P Polyethylene  (discontinued **) Polyethylene E6838-913P natural is a specialty formulation suggested for high-speed extrusion coating applications. E6838-913P offers improvements over standard low-density polyethylene in adhesion ..
Tensile Strength at Break	9.00 MPa	1310 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL WCD933 PPE-TPE Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN..
Tensile Strength at Break	9.00 MPa	1310 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCD933 PPE-TPE (Asia Pacific) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN..
Tensile Strength at Break	9.00 MPa	1310 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL WCD933 PPE-TPE (Asia Pacific) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN..
Tensile Strength at Break	9.00 MPa	1310 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCD933 PPE-TPE (Europe-Africa-Middle East) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN..
Tensile Strength at Break	9.00 MPa	1310 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL WCD933 PPE-TPE (Europe-Africa-Middle East) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN..
Tensile Strength at Break	9.00 MPa	1310 psi	500 mm/min; ASTM D638 - ISO 527-2
DuPont Elvaloy® 3427 AC Ethylene and 27% Butyl Acrylate Copolymer Elvaloy® 3427 AC can be used for coextrusion and compounding. It can also be used in extrusion coating. Elvaloy® 3427 AC is very soft and flexible, and has good adhesion to various polymers. It..
Tensile Strength at Break	9.00 MPa	1310 psi	500mm/min; ASTM D638 Type IV Specimen
Westlake EC4042AA Low Density Polyethylene WESTLAKE low-density polyethylene EC4042 is a low density resin designed for applications, such as sugar pouches and freezer wrap, where high coating speeds and good drawdown are required. The combi..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
ELASTO UK Dryflex® 422351S SBS Based Material, 35D Hardness, Black The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
ELASTO UK Dryflex® 500700S SEBS Based Material, Unfilled Qualities, 70A Hardness, Translucent The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
ELASTO UK Dryflex® 502700S SEBS Based Material, Unfilled Qualities, 70A Hardness, Black The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
ELASTO UK Dryflex® 602800S SEBS Based Material, Filled Qualities, 80A Hardness, Black The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material ..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
ELASTO UK Dryflex® 662750S SEBS Based Material, Semi-Filled Qualities, 75A Hardness, Black The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
ELASTO UK Dryflex® 662800S SEBS Based Material, Semi-Filled Qualities, 80A Hardness, Black The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t..
Tensile Strength at Break	9.03 MPa	1310 psi	Across Flow; ASTM D412
ExxonMobil Geolast® 701-87W183 Thermoplastic Elastomer A hard, black, oil resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good hot air and hot oil resistance for use in a wide range of applic..
Tensile Strength at Break	9.00 MPa	1310 psi	ISO R 527
Fainplast Compounds GS 55/AT Flexible PVC, Injection Molding for Transparent Technical Items Toys
Tensile Strength at Break	9.00 MPa	1310 psi	ISO R 527
Fainplast Compounds GS 58/O Flexible PVC, Injection Molding for Footwear Antislip soles, opaque surface
Tensile Strength at Break	9.00 MPa	1310 psi	ISO R 527
Fainplast Compounds GS 6802 Flexible PVC, Injection Molding for Footwear Soles
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
Arkema Group EVATANE® 33-45 Copolymer Ethylene - Vinyl Acetate EVATANE® 33-45 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 33-45 is stabilized with antioxidants. The High Vinyl Acetate co..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
Arkema Group LOTADER® 4503 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 4503 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized by high-pressure autoclave process.LOTADER 4503 is a versatile adhesive for extrusion lamination, des..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM-D638
Braskem IF33 LLDPE Injection Molding Polyethylene Copolymer IF33 is a linear low-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high fluidity, good flexibility, ..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
Azdel SuperLite® SL551200-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL551200-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic..
Tensile Strength at Break	9.00 MPa	1310 psi	ISO R 527
Fainplast Compounds PM 85/M Flexible PVC, Extrusion Cheap profiles