- Polymer Property : Tensile Strength at Break = 44.0 MPa
Polymer Property : Tensile Strength at Break = 44.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycoloy® C7240P PC+ABS (Asia Pacific) Cycoloy* C7240P resin is a mineral filled, flame retardant PC/ABS. High stiffness combined with balanced flow and impact performance, makes it a good condidate for various applications. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycoloy® C7410 PC+ABS (Asia Pacific) Cycoloy* C7410 resin is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® CX5430 PC+ABS Cycoloy* resin CX5430 is a general purpose PC/ABS blend developed for thin wall applications requiring weld line strength, high flow and impact together with a good balance of other properties. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Cycoloy® FXC810MA PC+ABS FXC810MA is the grade code for the Marble effect in PC/ABS. Marble is part of the VisualFX portfolio, and it is offered in a range of colors simluating the Marble effect. High heat/good flow charact.. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycoloy® MC1300 PC+ABS Cycoloy MC1300 resin is an injection moldable PC/ABS blend with excellent flow and impact performance. It is designed for plating applications mostly used in the automotive industry. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics GELOY FXW750SK ASA+PC Sparkle Metallic VisualFx ASA+PC Resin - Med. Heat & Impact Resin |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics GELOY XP7550 ASA+PC (Asia Pacific) Injection molding ASA-PC Blend suitable for exterior applications featuring outdoor weatherability, toughness, good heat performance and excellent flow. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® EXL4419 PC Copolymer (Asia Pacific) Lexan* EXL4419 polycarbonate (PC) siloxane copolymer resin is a 9% Glass Fiber (GF) reinforced opaque injection molding (IM) grade. This medium flow resin offers much higher ductility, improved rele.. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® EXL5689 PC Copolymer (Asia Pacific) Lexan* EXL5689 polycarbonate (PC) resin is a GF reinforced, UV stabilized, flame retardant injection molding copolymer blend. This medium flow resin features UL94 V0 @ 1.5mm flame retardancy based .. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® ML7667 PC Copolymer Lexan* ML7667 specialty polycarbonate (PC) resin is a 9% GF reinforced, UV stabilized, flame retarded injection molding grade. This medium flow specialty PC resin combines UL94 V0 @ 1.5mm, 5VB @ 3.. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® CX5430 PC+ABS (Europe-Africa-Middle East) Cycoloy* resin CX5430 is a general purpose PC/ABS blend developed for thin wall applications requiring weld line strength, high flow and impact together with a good balance of other properties.This .. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycoloy® FXC810SK PC+ABS Color package may affect performance. Visual Fx PC+ABS in various metallic (sparkle) colors. High heat/good flow characteristics. Appliance/automotive/telecommunication uses. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics GELOY XP7550 ASA+PC Injection molding ASA-PC Blend suitable for exterior applications featuring outdoor weatherability, toughness, good heat performance and excellent flow. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics GELOY XP7550 ASA+PC (Europe-Africa-Middle East) Injection molding ASA-PC Blend suitable for exterior applications featuring outdoor weatherability, toughness, good heat performance and excellent flow. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP IBP34 PA6.12 LNP* LUBRICOMP* IBP34 is a compound based on Nylon 6/12 containing 20% Glass Bead, 15% PTFE/Silicone. Added features include: Wear Resistant. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | ISO 527 Type 1A |
| Solvay TECHNYL® A 258 PA Black 2N PA66, DRY Description: Unreinforced and modified polyamide 66, UV and thermal stabilized with excellent impact resistance, for injection molding.Available in: Europe Product Applications: TECHNYL® A 258P1 .. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® CL101 PBT+PC (Europe-Africa-Middle East) Xenoy CL101 is an unfilled, impact modified PC/PBT blend with excellent solvent resistance and low-temperature ductility. It has a proven track record in off-line painted exterior automotive applica.. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | ISO R 527 |
| Stir SpA RS 18 (PVC) Application: Molding for bends, connections and electrical fittings for buildingInformation provided by STIR SpA |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | ISO 527-1/-2 |
| Styrolution Polystyrol 145 D PS Description: Polystyrol 145 D is a medium strength, easy flowing general purpose grade, suitable for blending with impact modified Polystyrol.Applications: In blends with high impact polystyrene esp.. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Noryl N750T PPE+HIPS ECO-FLO(tm). ECO conforming, nonhalogenated flame retardant PPE+PS. High flow. Electrical, TV and Business equipment applications.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® V3903WX PBT+PC (Asia Pacific) Unreinforced fllame retardant PBT/PC blends with good chemical resistance and low temperature impact, UV stablized |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP MF002S PP LNP* Thermocomp* MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 87% Ret. |
| UBE UBESTA® 3030U Nylon 12 (After Xylene for 1000 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c.. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | ISO 527-1/-2 |
| DuPont Performance Polymers Hytrel® HTR8163HVBK Polyester Elastomer TPC-ET
(Unverified Data**) 65 Shore D Polyester Elastomer with Heat Ageing Protection Developed for ExtrusionInformation provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
| Arkema Group Pebax® MV 1041 SA 01 Polyether Block Amide (PEBA) Polyether block amide PEBAX® MV 1041 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This hydrophilic grade when extruded into either a thin film or laminated on .. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | ASTM D638 |
| Azdel SuperLite® SL550600-100 PP Resin Matrix / 55% Glass Fiber (1 mm Molded Thickness) AZDEL SuperLite® SL550600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | ISO 527-1 |
| Barlog Plastics KEBAFORM C 904 GB POM Copolymer, 20% glass bead reinforced POM-GB20Information provided by BARLOG plastics GmbH. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® EXL5689 PC Copolymer Lexan* EXL5689 polycarbonate (PC) resin is a GF reinforced, UV stabilized, flame retardant injection molding copolymer blend. This medium flow resin features UL94 V0 @ 1.5mm flame retardancy based .. |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermotuf PX08000 PA 6 (Europe-Africa-Middle East) LNP* THERMOTUF* PX08000 is a compound based on PA6 resin containing Impact Modifier. Added features include : High Impact.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region... |
|||
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics GELOY XP4025 ASA+PC Available in a wide range of colors and is recommended for unpainted exterior applications. |
|||