Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 30.0 - 50.0 MPa | 4350 - 7250 psi | Compression; ISO 527 |
Raschig Group 6501 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Tensile Strength, Yield | 30.0 - 50.0 MPa | 4350 - 7250 psi | Compression; ISO 527 |
Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve.. |
|||
Tensile Strength, Yield | 30.0 - 50.0 MPa | 4350 - 7250 psi | Compression; ISO 527 |
Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat.. |
|||
Tensile Strength, Yield | 30.0 - 50.0 MPa | 4350 - 7250 psi | Compression; ISO 527 |
Raschig Group AMPLA® 7250 melamine-modified polyester Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow.. |
|||
Tensile Strength, Yield | 30.0 - 50.0 MPa | 4350 - 7250 psi | Compression; ISO 527 |
Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta.. |
|||
Tensile Strength, Yield | 30.0 - 50.0 MPa | 4350 - 7250 psi | Injection and Compression; ISO 527 |
Raschig Group EPOXIDUR® 3580 EP Epoxy Glass-fiber reinforced and mineral filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties even with thin wall thicknesses and high temperatures. This prod.. |
|||
Tensile Strength, Yield | 40.0 - 50.0 MPa | 5800 - 7250 psi | Compression; ISO 527 |
Raschig Group MELOPLAS® 150 MF Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr.. |
|||
Tensile Strength, Yield | 42.0 - 50.0 MPa | 6090 - 7250 psi | Average value: 46.6 MPa Grade Count:18 |
Overview of materials for PCTG Copolyester This property data is a summary of similar materials in the MatWeb database for the category "PCTG Copolyester". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Tensile Strength, Yield | 30.0 - 50.0 MPa @Temperature 120 - 200 °C |
4350 - 7250 psi @Temperature 248 - 392 °F |
Average value: 38.8 MPa Grade Count:2 |
Overview of materials for Nylon 46, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Tensile Strength, Yield | 39.0 - 50.0 MPa | 5660 - 7250 psi | Average value: 44.8 MPa Grade Count:4 |
Overview of materials for Nylon 12, Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Graphite Filled". Each property range of values reported is minimum and maximum values of appr.. |
|||
Tensile Strength, Yield | 48.0 - 50.0 MPa | 6960 - 7250 psi | ASTM D638 |
3D Systems Accura® 50 Plastic for SLA® Systems Simulate the properties and appearance of molded ABS. For use with the Viper™ SLA® system, SLA 3500, SLA 5000 and SLA 7000 systems.ApplicationsFunctional components for assemblies, mock-ups and te.. |
|||
Tensile Strength, Yield | 34.0 - 50.0 MPa | 4930 - 7250 psi | ASTM D638 |
Arkema Group VOLTALEF® 300 HD PCTFE VOLTALEF® 300 HD is a chlorotrifluoroethylene powder. Used for compression molding, very good flow, non-flammable. Information provided by Arkema Group |
|||
Tensile Strength, Yield | 34.0 - 50.0 MPa | 4930 - 7250 psi | ASTM D638 |
Arkema Group VOLTALEF® 302 PCTFE VOLTALEF® 302 is a chlorotrifluoroethylene dense powder. Used in particular for compression molding, non-flammable. Information provided by Arkema Group |